SwePub - sökning: id:"swepub:oai:research.chalme...

Numrering	Referens	Omslagsbild	Hitta
1.	Barreto, C., et al. (författare) Multiwall carbon nanotube/PPC composites: Preparation, structural analysis and thermal stability 2013 Ingår i: European Polymer Journal. - : Elsevier BV. - 0014-3057 .- 1873-1945. ; 49:8, s. 2149-2161 Tidskriftsartikel (refereegranskat)abstract The focus of this report concerns the preparation nanocomposites from poly(propylene carbonate) (PPC) and multiwall carbon nanotubes (MWNTs). A solvent route using tetrahydrofuran, ethoxylated non- ionic surfactants combined with sonication was found to be successful in deagglomerating and dispersing the nanotubes. Transmission electron microscopy revealed highly disentangled and dispersed nanotubes and was supported by the qualitative stability evaluations. The morphology and molecular mobility of the prepared nanocomposites (0.5, 3.0 and 5.0 wt% of nanotubes) were characterized by rheology, microscopy, low-field solid-state nuclear magnetic resonance, and electrical conductivity. The networking of nanotubes was highest with a stearyl alcohol ethoxylate surfactant, and was found to improve with the sonication time. Nanotube percolation was established, both rheologically and electrically, from a filler content of approximately 0.5 wt%. A higher tendency toward particle agglomeration was observed at higher MWNT loadings. Only minor changes in the glass transition temperature were measured presumably due to the presence of solvent and surfactant residues. The thermal stability was marginally improved by increasing the loading and dispersion of the nanotubes, and appeared to be modified by solvent and surfactant residues.

Barreto, C., et al. (författare)
Multiwall carbon nanotube/PPC composites: Preparation, structural analysis and thermal stability
2013
Ingår i: European Polymer Journal. - : Elsevier BV. - 0014-3057 .- 1873-1945. ; 49:8, s. 2149-2161
Tidskriftsartikel (refereegranskat)abstract
- The focus of this report concerns the preparation nanocomposites from poly(propylene carbonate) (PPC) and multiwall carbon nanotubes (MWNTs). A solvent route using tetrahydrofuran, ethoxylated non- ionic surfactants combined with sonication was found to be successful in deagglomerating and dispersing the nanotubes. Transmission electron microscopy revealed highly disentangled and dispersed nanotubes and was supported by the qualitative stability evaluations. The morphology and molecular mobility of the prepared nanocomposites (0.5, 3.0 and 5.0 wt% of nanotubes) were characterized by rheology, microscopy, low-field solid-state nuclear magnetic resonance, and electrical conductivity. The networking of nanotubes was highest with a stearyl alcohol ethoxylate surfactant, and was found to improve with the sonication time. Nanotube percolation was established, both rheologically and electrically, from a filler content of approximately 0.5 wt%. A higher tendency toward particle agglomeration was observed at higher MWNT loadings. Only minor changes in the glass transition temperature were measured presumably due to the presence of solvent and surfactant residues. The thermal stability was marginally improved by increasing the loading and dispersion of the nanotubes, and appeared to be modified by solvent and surfactant residues.

Träfflista för sökning "id:"swepub:oai:research.chalmers.se:264ddb8e-e069-407b-952d-3918f0bc11c2" "

Avgränsa träffmängd