- Okada, S, et al.
(författare)
-
Crystal growth and some properties of LuB4, LuAlB4, and Lu2AlB6
- 1996
-
Ingår i: JAPANESE JOURNAL OF APPLIED PHYSICS PART 1-REGULAR PAPERS SHORT NOTES & REVIEW PAPERS. - : JAPAN J APPLIED PHYSICS. ; 35:9A
-
Annan publikation (övrigt vetenskapligt/konstnärligt)abstract
- Crystals of LuB4, LuAlB4, and Lu2AlB6 were grown by the high-temperature aluminium solution method using lutetium oxide and crystalline boron powders as starting materials. The growth conditions for obtaining single crystals of relatively large size were
|
|
7. |
- Okada, S, et al.
(författare)
-
Crystal growth of vanadium silicides from high-temperature metal solutions and some properties of the crystals
- 1996
-
Ingår i: MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING. - : ELSEVIER SCIENCE SA LAUSANNE. ; 209:1-2
-
Annan publikation (övrigt vetenskapligt/konstnärligt)abstract
- Crystals of vanadium silicides were grown from high-temperature tin and copper solutions in an argon atmosphere using vanadium metal chips and silicon powder as starting materials. The crystals grown were V3Si, V5Si3 and VSi2. The growth conditions for o
|
|
8. |
- OKADA, S, et al.
(författare)
-
PREPARATIONS AND SOME PROPERTIES OF W2B, DELTA-WB AND WB2 CRYSTALS FROM HIGH-TEMPERATURE METAL SOLUTIONS
- 1995
-
Ingår i: JAPANESE JOURNAL OF APPLIED PHYSICS PART 1-REGULAR PAPERS SHORT NOTES & REVIEW PAPERS. - : JAPAN J APPLIED PHYSICS. ; 34:1
-
Annan publikation (övrigt vetenskapligt/konstnärligt)abstract
- W2B, delta-WB and WB2 crystals were preparad from high temperature aluminium and copper solutions using tungsten metal and crystalline boron powders as starting material under an argon atmosphere. Growth conditions for obtaining crystals of relatively la
|
|
9. |
|
|
10. |
- YU, Y, et al.
(författare)
-
A STRUCTURAL INVESTIGATION OF V2B3 BY SINGLE-CRYSTAL DIFFRACTOMETRY
- 1995
-
Ingår i: JOURNAL OF ALLOYS AND COMPOUNDS. - : ELSEVIER SCIENCE SA LAUSANNE. ; 221
-
Annan publikation (övrigt vetenskapligt/konstnärligt)abstract
- The crystal structure of V2B3 was reinvestigated using single-crystal X-ray diffractometry. V2B3 crystallizes in the orthorhombic space group Cmcm with a = 3.0599(4) Angstrom, b = 18.429(2) Angstrom, c = 2.9839(4) Angstrom, Z = 4. The crystal was grown f
|
|