1. |
- Kim, Seong-Min, et al.
(författare)
-
Influence of PEDOT:PSS crystallinity and composition on electrochemical transistor performance and long-term stability
- 2018
-
Ingår i: Nature Communications. - : NATURE PUBLISHING GROUP. - 2041-1723. ; 9
-
Tidskriftsartikel (refereegranskat)abstract
- Owing to the mixed electron/hole and ion transport in the aqueous environment, poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate)-based organic electrochemical transistor has been regarded as one of the most promising device platforms for bioelectronics. Nonetheless, there exist very few in-depth studies on how intrinsic channel material properties affect their performance and long-term stability in aqueous environments. Herein, we investigated the correlation among film microstructural crystallinity/composition, device performance, and aqueous stability in poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) films. The highly organized anisotropic ordering in crystallized conducting polymer films led to remarkable device characteristics such as large transconductance (similar to 20 mS), extraordinary volumetric capacitance (113 F.cm(-3)), and unprecedentedly high [mu C*] value (similar to 490 F.cm(-1) V-1 s(-1)). Simultaneously, minimized poly(styrenesulfonate) residues in the crystallized film substantially afforded marginal film swelling and robust operational stability even after amp;gt;20-day water immersion, amp;gt;2000-time repeated on-off switching, or high-temperature/pressure sterilization. We expect that the present study will contribute to the development of long-term stable implantable bioelectronics for neural recording/stimulation.
|
|
2. |
- Kim, Seong-Min, et al.
(författare)
-
High-performance, polymer-based direct cellular interfaces for electrical stimulation and recording
- 2018
-
Ingår i: NPG ASIA MATERIALS. - : NATURE PUBLISHING GROUP. - 1884-4049 .- 1884-4057. ; 10, s. 255-265
-
Tidskriftsartikel (refereegranskat)abstract
- Due to the trade-off between their electrical/electrochemical performance and underwater stability, realizing polymer-based, high-performance direct cellular interfaces for electrical stimulation and recording has been very challenging. Herein, we developed transparent and conductive direct cellular interfaces based on a water-stable, high-performance poly(3,4-ethylenedioxythiophene):polystyrene sulfonate (PEDOT:PSS) film via solvent-assisted crystallization. The crystallized PEDOT:PSS on a polyethylene terephthalate (PET) substrate exhibited excellent electrical/electrochemical/optical characteristics, long-term underwater stability without film dissolution/delamination, and good viability for primarily cultured cardiomyocytes and neurons over several weeks. Furthermore, the highly crystallized, nanofibrillar PEDOT:PSS networks enabled dramatically enlarged surface areas and electrochemical activities, which were successfully employed to modulate cardiomyocyte beating via direct electrical stimulation. Finally, the high-performance PEDOT:PSS layer was seamlessly incorporated into transparent microelectrode arrays for efficient, real-time recording of cardiomyocyte action potentials with a high signal fidelity. All these results demonstrate the strong potential of crystallized PEDOT:PSS as a crucial component for a variety of versatile bioelectronic interfaces.
|
|