1. |
- Ehman, N. V., et al.
(author)
-
Influence of initial chemical composition and characteristics of pulps on the production and properties of lignocellulosic nanofibers
- 2020
-
In: International Journal of Biological Macromolecules. - : Elsevier B.V.. - 0141-8130 .- 1879-0003. ; 143, s. 453-461
-
Journal article (peer-reviewed)abstract
- This work aimed to study the influence of the initial chemical composition (glucans, lignin, xylan, and mannans), intrinsic viscosity, and carboxylate groups of pulps on the production process and final properties of lignocellulosic nanofibers (LCNF). Pulps of pine sawdust, eucalyptus sawdust, and sugarcane bagasse subjected to conventional pulping and highly oxidized processes were the starting materials. The LCNF were obtained by TEMPO mediated oxidation and mechanical fibrillation with a colloidal grinder. The nanofibrillation degree, chemical charge content, rheology, laser profilometry, cristallinity and atomic force microscopy were used to characterize the LCNF. The carboxylate groups, hemicelluloses and lignin of the initial pulps were important factors that affected the production process of LCNF. The results revealed that intrinsic viscosity and carboxylate groups of the initial pulps affected LCNF production process, whereas lignin and hemicelluloses influenced the viscosity of LCNF aqueous suspensions, the roughness of LCNF films, and the carboxylate groups content of LCNF
|
|
2. |
- Gamelas, José A. F., et al.
(author)
-
On the morphology of cellulose nanofibrils obtained by TEMPO-mediated oxidation and mechanical treatment
- 2015
-
In: Micron. - : Elsevier BV. - 0968-4328 .- 1878-4291. ; 72, s. 28-33
-
Journal article (peer-reviewed)abstract
- The morphological properties of cellulose nanofibrils obtained from eucalyptus pulp fibres were assessed. Two samples were produced with the same chemical treatment (NaClO/NaBr/TEMPO (2,2,6,6-tetramethylpiperidine-1-oxyl radical) oxidation), but distinct mechanical treatment intensities during homogenization. It was shown that the nanofibrils production yield increases with the mechanical energy. The effect of mechanical treatment on the yield was confirmed by laser profilometry of air-dried nanocellulose films. However, no significant differences were detected regarding the nanofibrils width as measured by atomic force microscopy (AFM) of air-dried films. On the other hand, differences in size were found either by laser diffraction spectroscopy or by dynamic light scattering (DLS) of the cellulose nanofibrils suspensions as a consequence of the differences in the length distribution of both samples. The nanofibrils length of the more nanofibrillated sample was calculated based on the width measured by AFM and the hydrodynamic diameter obtained by DLS. A length value of ca. 600. nm was estimated. The DLS hydrodynamic diameter, as an equivalent spherical diameter, was used to estimate the nanofibrils length assuming a cylinder with the same volume and with the diameter (width) assessed by AFM. A simple method is thus proposed to evaluate the cellulose nanofibrils length combining microscopy and light scattering methods.
|
|
3. |
|
|