New hemicellulose-based hydrogels
-
- Lindblad, M. S. (författare)
- KTH,Fiber- och polymerteknologi
-
- Albertsson, Ann-Christine (författare)
- KTH,Polymerteknologi
-
- Ranucci, Elisabetta (författare)
- KTH,Fiber- och polymerteknologi
-
(creator_code:org_t)
- WASHINGTON : AMER CHEMICAL SOC, 2004
- 2004
- Engelska.
-
Ingår i: HEMICELLULOSES: SCIENCE AND TECHNOLOGY. - WASHINGTON : AMER CHEMICAL SOC. - 0841238421 ; , s. 347-359
- Relaterad länk:
-
https://urn.kb.se/re...
Abstract
Ämnesord
Stäng
- Different kinds of hemicellulose-based hydrogels have been made by radical polymerization using hydrosoluble hemicellulose from spruce chips with a number-average molecular weight and polydispersity of 2400 and 1.5 respectively. 80% of the hemicellulose was galactoglucomannan. and the remainder mainly 4-O-methylglucuronoxylan. Hemicellulose/poly(2-hydroxyethyl methacrylate) based hydrogels were prepared by polymerization in water of 2-hydroxyethyl methacrylate with hemicellulose modified with well-defined amounts of methacrylic functions. The chemical modification of hemicellulose was performed in dimethyl sulfoxide using 2[(l-imidazolyl) formyloxy]ethyl methacrylate as modifying agent. The kinetics of the modification reaction were monitored by H-1 NMR. The degree of modification of the hemicellulose used for the hydrogel synthesis varied from 10% to 40%. The ratio of modified hemicellulose to 2-hydroxyethyl methacrylate in the hydrogels was 1: 1 by weight. The resulting hydrogels were elastic, homogeneous, soft, transparent and easily swollen in water.
Ämnesord
- NATURVETENSKAP -- Kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences (hsv//eng)
Nyckelord
- dextran
- polymers
- wood
Publikations- och innehållstyp
- ref (ämneskategori)
- kon (ämneskategori)
Hitta via bibliotek
Till lärosätets databas