A novel face-centered-cubic high-entropy alloy strengthened by nanoscale precipitates
-
- Qin, Gang (författare)
- Harbin Inst Technol, Natl Key Lab Precis Hot Proc Met, Harbin 150001, Heilongjiang, Peoples R China.
-
- Chen, Ruirun (författare)
- Harbin Inst Technol, Natl Key Lab Precis Hot Proc Met, Harbin 150001, Heilongjiang, Peoples R China.;Harbin Inst Technol, State Key Lab Adv Welding & Joining, Harbin 150001, Heilongjiang, Peoples R China.
-
- Liaw, Peter K. (författare)
- Univ Tennessee, Dept Mat Sci & Engn, Knoxville, TN 37996 USA.
-
visa fler...
-
- Ga, Yanfei (författare)
- Univ Tennessee, Dept Mat Sci & Engn, Knoxville, TN 37996 USA.
-
- Li, Xiaoqing (författare)
- KTH,Materialvetenskap
-
- Zheng, Huiting (författare)
- Harbin Inst Technol, Natl Key Lab Precis Hot Proc Met, Harbin 150001, Heilongjiang, Peoples R China.
-
- Wang, Liang (författare)
- Harbin Inst Technol, Natl Key Lab Precis Hot Proc Met, Harbin 150001, Heilongjiang, Peoples R China.
-
- Su, Yanqing (författare)
- Harbin Inst Technol, Natl Key Lab Precis Hot Proc Met, Harbin 150001, Heilongjiang, Peoples R China.
-
- Guo, Jingjie (författare)
- Harbin Inst Technol, Natl Key Lab Precis Hot Proc Met, Harbin 150001, Heilongjiang, Peoples R China.
-
- Fu, Hengzhi (författare)
- Harbin Inst Technol, Natl Key Lab Precis Hot Proc Met, Harbin 150001, Heilongjiang, Peoples R China.
-
visa färre...
-
Harbin Inst Technol, Natl Key Lab Precis Hot Proc Met, Harbin 150001, Heilongjiang, Peoples R China Harbin Inst Technol, Natl Key Lab Precis Hot Proc Met, Harbin 150001, Heilongjiang, Peoples R China.;Harbin Inst Technol, State Key Lab Adv Welding & Joining, Harbin 150001, Heilongjiang, Peoples R China. (creator_code:org_t)
- PERGAMON-ELSEVIER SCIENCE LTD, 2019
- 2019
- Engelska.
-
Ingår i: Scripta Materialia. - : PERGAMON-ELSEVIER SCIENCE LTD. - 1359-6462 .- 1872-8456. ; 172, s. 51-55
- Relaterad länk:
-
https://www.scienced...
-
visa fler...
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- A new single-phase face-centered-cubic (FCC) Co9Cr7Cu36Mn25Ni23 [atomic percent, similar hereinafter] high-entropy alloy (HEA) was prepared by arc melting. A uniform distribution of nanometer-sized precipitates was achieved. The tensile yield strength, ultimate tensile strength, and elongation were 401 MPa, 700 MPa, and 36%, respectively. The energy-dispersive spectrometer results showed that the nano-precipitates were rich in Co and Cr elements. Moreover, the crystal-forming behavior and the nanoscale-precipitates-forming mechanism were revealed. Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
Nyckelord
- High-entropy alloys
- Nanoscale
- Mechanical properties
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Qin, Gang
-
Chen, Ruirun
-
Liaw, Peter K.
-
Ga, Yanfei
-
Li, Xiaoqing
-
Zheng, Huiting
-
visa fler...
-
Wang, Liang
-
Su, Yanqing
-
Guo, Jingjie
-
Fu, Hengzhi
-
visa färre...
- Om ämnet
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Materialteknik
- Artiklar i publikationen
-
Scripta Material ...
- Av lärosätet
-
Kungliga Tekniska Högskolan