Phosphorus partition between liquid steel and CaO-SiO2-P2O5-MgO slag containing low FeO
-
- Basu, Somnath (författare)
- KTH,Materialvetenskap
-
- Lahiri, Ashok Kumar (författare)
- KTH
-
- Seetharaman, Seshadri (författare)
- KTH,Materialens processvetenskap
-
(creator_code:org_t)
- 2007-06-15
- 2007
- Engelska.
-
Ingår i: Metallurgical and materials transactions. B, process metallurgy and materials processing science. - : Springer Science and Business Media LLC. - 1073-5615 .- 1543-1916. ; 38:3, s. 357-366
- Relaterad länk:
-
http://www.springerl...
-
visa fler...
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- CaO-SiO2-FeOx-P2O5-MgO bearing slags are typical in the basic oxygen steelmaking (BOS) process. The partition ratio of phosphorus between slag and steel is an index of the phosphorus holding capacity of the slag, which determines the phosphorus content achievable in the finished steel. The influences of FeO concentration and basicity on the equilibrium phosphorus partition ratios were experimentally determined at temperatures of 1873 and 1923 K, for conditions of MgO saturation. The partition ratio initially increased with basicity but attained a constant value beyond basicity of 2.5. An increase in FeO concentration up to approximately 13 to 14 mass pet was beneficial for phosphorus partition.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Nyckelord
- OXYGEN; STEELMAKING; SYSTEM; METAL; IRON
- Metallurgical process engineering
- Metallurgisk processteknik
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas