Unintentional carbide formation evidenced during high-vacuum magnetron sputtering of transition metal nitride thin films
-
- Greczynski, Grzegorz (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten,Rhein Westfal TH Aachen, Germany
-
- Mraz, S. (författare)
- Rhein Westfal TH Aachen, Germany
-
- Hultman, Lars (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten
-
visa fler...
-
- Schneider, J. M. (författare)
- Rhein Westfal TH Aachen, Germany
-
visa färre...
-
(creator_code:org_t)
- ELSEVIER SCIENCE BV, 2016
- 2016
- Engelska.
-
Ingår i: Applied Surface Science. - : ELSEVIER SCIENCE BV. - 0169-4332 .- 1873-5584. ; 385, s. 356-359
- Relaterad länk:
-
https://liu.diva-por... (primary) (Raw object)
-
visa fler...
-
http://liu.diva-port...
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Carbide signatures are ubiquitous in the surface analyses of industrially sputter-deposited transition metal nitride thin films grown with carbon-less source materials in typical high-vacuum systems. We use high-energy-resolution photoelectron spectroscopy to reveal details of carbon temporal chemical state evolution, from carbide formed during film growth to adventitious carbon adsorbed upon contact with air. Using in-situ grown Al capping layers that protect the as-deposited transition metal nitride surfaces from oxidation, it is shown that the carbide forms during film growth rather than as a result of post deposition atmosphere exposure. The XPS signature of carbides is masked by the presence of adventitious carbon contamination, appearing as soon as samples are exposed to atmosphere, and eventually disappears after one week-long storage in lab atmosphere. The concentration of carbon assigned to carbide species varies from 0.28 at% for ZrN sample, to 0.25 and 0.11 at% for TiN and HfN, respectively. These findings are relevant for numerous applications, as unintentionally formed impurity phases may dramatically alter catalytic activity, charge transport and mechanical properties by offsetting the onset of thermally induced phase transitions. Therefore, the chemical state of C impurities in PVD-grown films should be carefully investigated. (C) 2016 Elsevier B.V. All rights reserved.
Ämnesord
- NATURVETENSKAP -- Kemi -- Materialkemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Materials Chemistry (hsv//eng)
Nyckelord
- XPS; Surface chemistry; Magnetron sputtering; Carbon; Titanium nitride