Modeling and simulations of Pd/n-ZnO Schottky diode and its comparison with measurements
-
- Muniza Faraz, Sadia (författare)
- Linköpings universitet,Institutionen för fysik, kemi och biologi,Tekniska högskolan
-
- Noor, Hadia (författare)
- Department of Physics, Islamia University of Bahawalpur, Pakistan
-
- Asghar, M. (författare)
- Department of Physics, Islamia University of Bahawalpur, Pakistan
-
visa fler...
-
- Willander, Magnus (författare)
- Linköpings universitet,Institutionen för teknik och naturvetenskap,Tekniska högskolan
-
- Wahab, Qamar ul (författare)
- Linköpings universitet,Halvledarmaterial,Tekniska högskolan
-
visa färre...
-
(creator_code:org_t)
- 2009
- 2009
- Engelska.
-
Ingår i: Advanced Materials Research. - 1662-8985. ; 79-82, s. 1317-1320
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.4...
-
visa färre...
Abstract
Ämnesord
Stäng
- Modeling of Pd/ZnO Schottky diode has been performed together with a set of simulations to investigate its behavior in current-voltage characteristics. The diode was first fabricated and then the simulations were performed to match the IV curves to investigate the possible defects and their states in the bandgap. The doping concentration measured by capacitancevoltage is 3.4 x 1017 cm-3. The Schottky diode is simulated at room temperature and the effective barrier height is determined from current voltage characteristics both by measurements and simulations and it was found to be 0.68eV. The ideality factor obtained from simulated results is 1.06-2.04 which indicates that the transport mechanism is thermionic. It was found that the recombination current in the depletion region is responsible for deviation of experimental values from the ideal thermionic model deployed by the simulator.
Nyckelord
- ZnO
- Schottky contact
- Barrier height
- NATURAL SCIENCES
- NATURVETENSKAP
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas