Solidification behaviour and phase constituents of cast Mg-Zn-misch metal alloys

• The solidification path and phase constituents of alloys in the magnesium-rich corner of the Mg-Zn-misch metal (MM) pseudo-ternary system have been investigated by a combination of differential thermal analysis, analytical electron microscopy and X-ray diffraction. The solidification behaviour diagram for this system was found to be dominated by a large two-phase ( -Mg plus T-phase) field in which the lowest eutectic temperature was 500°C. T-phase has a c-centred orthorhombic crystal structure and exhibits a wide range of stoichiometry. The interdendritic eutectic phase in the pseudo-binary Mg-MM system is Mg12MM which has the same b c t structure as Mg12Ce. The eutectic temperature here is 593°C.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Annan materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Other Materials Engineering (hsv//eng)

Nyckelord

Material Mechanics

Materialmekanik

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)