Edgren, Aina,1995Chalmers University of Technology, Gothenburg, SE-41296, Sweden; Kanthal AB, Hallstahammar, SE-73427, Sweden,Chalmers tekniska högskola,Kanthal AB
(författare)
High temperature compression of Mo(Si,Al)2-Al2O3 composites
- Artikel/kapitelEngelska2023
Förlag, utgivningsår, omfång ...
-
Elsevier,2023
-
electronicrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:ltu-95494
-
https://urn.kb.se/resolve?urn=urn:nbn:se:ltu:diva-95494URI
-
https://doi.org/10.1016/j.msea.2023.144583DOI
-
https://research.chalmers.se/publication/534319URI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
Validerad;2023;Nivå 2;2023-04-12 (sofila);Funder: Kanthal AB (grant no. ID18-0064.)
-
The aim of this study was to investigate the effect on high temperature of mechanical properties of adding Al2O3 particles to polycrystalline Mo(Si,Al)2. Mo(Si,Al)2-Al2O3 composites, containing 0–25 wt% Al2O3 particles have been compression tested at 1300 °C, and the microstructure after deformation was studied using electron backscatter diffraction. It was shown that even small amounts (5 wt%) of Al2O3 particles resulted in a grain-refined material through inhibition of grain growth during sintering, which lead to lower flow stresses compared to the coarse-grained Al2O3-free material. The inverse grain size effect and post-test microstructure investigations suggest that creep-like deformation mechanisms dominate in fine grained Mo(Si,Al)2-Al2O3 composites at 1300 °C. In the materials containing 5–15 wt% Al2O3, the maximum stress decreased with increasing Al2O3 content. In materials with higher Al2O3 additions, the maximum stress increased with the Al2O3 addition, but did not reach the strength levels in the Al2O3-free reference material. It is suggested that the deformation behaviour is affected by electroplasticity effects as resistive heating was used. Electroplasticity contributes to the decrease in maximum stress observed in the lower Al2O3 containing materials, while this is outweighed by particle strengthening at higher Al2O3 contents.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Ström, ErikKanthal AB, Hallstahammar, SE-73427, Sweden
(författare)
-
Frisk, LarsLuleå tekniska universitet,Materialvetenskap,Luleå tekniska universitet (LTU),Luleå University of Technology (LTU)(Swepub:ltu)larfri
(författare)
-
Akhtar, FaridLuleå tekniska universitet,Materialvetenskap,Luleå tekniska universitet (LTU),Luleå University of Technology (LTU)(Swepub:ltu)farakh
(författare)
-
Hörnqvist Colliander, Magnus,1979Chalmers University of Technology, Gothenburg, SE-41296, Sweden,Chalmers tekniska högskola(Swepub:cth)magnuh
(författare)
-
Chalmers University of Technology, Gothenburg, SE-41296, Sweden; Kanthal AB, Hallstahammar, SE-73427, SwedenChalmers tekniska högskola
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Materials Science & Engineering: Elsevier8650921-50931873-4936
Internetlänk
Hitta via bibliotek
Till lärosätets databas