Effect of capillary condensation on friction force and adhesion
-
- Feiler, Adam (författare)
- KTH,Uppsala universitet,RISE,YKI – Ytkemiska institutet,Centrum för ytbioteknik,Ytkemi
-
- Stiernstedt, Johanna (författare)
- KTH,RISE,YKI – Ytkemiska institutet,Ytkemi
-
- Theander, Katarina (författare)
- KTH,RISE,YKI – Ytkemiska institutet,Ytkemi
-
visa fler...
-
Jenkins, P (författare)
-
- Rutland, Mark (författare)
- KTH,RISE,YKI – Ytkemiska institutet,Ytkemi
-
visa färre...
-
(creator_code:org_t)
- American Chemical Society (ACS), 2007
- 2007
- Engelska.
-
Ingår i: Langmuir. - : American Chemical Society (ACS). - 0743-7463 .- 1520-5827. ; 23:2, s. 517-522
- Relaterad länk:
-
http://pubs3.acs.org...
-
visa fler...
-
https://urn.kb.se/re...
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
https://urn.kb.se/re...
-
visa färre...
Abstract
Ämnesord
Stäng
- Friction force measurements have been conducted with a colloid probe on mica and silica (both hydrophilic and hydrophobised) after long (24 hour) exposure to high humidity air. Adhesion and friction measurements have also been performed on cellulose substrates. The long exposure to high humidity led to a large hysteresis between loading and unloading in the friction measurements with separation occurring at large negative applied loads. The large hysteresis in the friction-load relationship is attributed to a contact area hysteresis of the capillary condensate which built up during loading and did not evaporate during the unloading regime. The magnitude of the friction force varied dramatically between substrates and was lowest on the mica substrate and highest on the hydrophilic silica substrate with the hydrophobised silica and cellulose being intermediate. The adhesion due to capillary forces on cellulose was small compared to that on the other substrates, due to the greater roughness of these surfaces.
Ämnesord
- NATURVETENSKAP -- Kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences (hsv//eng)
Nyckelord
- Friction
- capillary condensation
- cellulose
- mica
- silica
- atomic force microscopy
- AFM
- surface force
- adhesion
- paper
- humidity
- colloid probe
- nanotribology.
- Chemistry
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
-
Langmuir
(Sök värdpublikationen i LIBRIS)
Till lärosätets databas