Cation field-strength effects on ion irradiation-induced mechanical property changes of borosilicate glass structures
-
- Lv, Zhong-Peng (författare)
- Stockholms universitet,Institutionen för material- och miljökemi (MMK),Lanzhou University, China
-
Sun, Zhao (författare)
-
Wang, Fugang (författare)
-
visa fler...
-
- Yu, Yang, 1987- (författare)
- Stockholms universitet,Institutionen för material- och miljökemi (MMK)
-
Yang, Fan (författare)
-
Yue, Shengjun (författare)
-
- Edén, Mattias (författare)
- Stockholms universitet,Avdelningen för fysikalisk kemi,Lanzhou University, China
-
Chen, Liang (författare)
-
Wang, Tieshan (författare)
-
visa färre...
-
(creator_code:org_t)
- 2023
- 2023
- Engelska.
-
Ingår i: Journal of The American Ceramic Society. - 0002-7820 .- 1551-2916. ; 106:10, s. 5766-5780
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- We examine the impact of the glass network-modifier cation field strength (CFS) on ion irradiation-induced mechanical property changes in borosilicate (BS) glasses for the ternary M2O-B2O3-SiO2 systems with M = {Na, K, Rb} and the quaternary [0.5M((2))O-0.5Na(2)O]-B2O3-SiO2 systems with M = {Li, Na, K, Rb Mg, Ca, Sr, Ba}. B-11 nuclear magnetic resonance (NMR) experiments on the as-prepared BS glasses yielded the fractional population of four-coordinated B species (B-[4]) out of all {B-[3], B-[4]} groups in the glass network, along with the fraction of B-[4]-O-Si linkages out of all B-[4]-O-Si/B bonds. Both parameters correlated linearly with the (average) CFS of the M+ and/or {M(2)+, Na+} cations. Both the nanoindentation-derived hardness and Young's modulus values of the glasses reduced upon their irradiation by Si2+ ions, with the property deterioration decreasing linearly with increasing Mz+ CFS, that is, for higher Mz+center dot center dot center dot O interaction strength. The irradiation damage of the glass network also increased linearly with the fraction of B-[4]-O-Si linkages, which are the second weakest in the structure after the Mz+center dot center dot center dot O bonds. Our results underscore the advantages of employing BS glasses with high-CFS cations for enhancing the radiation resistance for nuclear waste storage.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
Nyckelord
- B-11 MAS NMR
- borosilicate glass
- composition-structure-property correlations
- ion irradiation
- mechanical properties
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Lv, Zhong-Peng
-
Sun, Zhao
-
Wang, Fugang
-
Yu, Yang, 1987-
-
Yang, Fan
-
Yue, Shengjun
-
visa fler...
-
Edén, Mattias
-
Chen, Liang
-
Wang, Tieshan
-
visa färre...
- Om ämnet
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Materialteknik
- Artiklar i publikationen
-
Journal of The A ...
- Av lärosätet
-
Stockholms universitet