Nanosilicon Electrodes for Lithium-Ion Batteries : Interfacial Mechanisms Studied by Hard and Soft X-ray Photoelectron Spectroscopy
-
- Philippe, Bertrand (författare)
- Uppsala universitet,Strukturkemi
-
- Dedryvere, Remi (författare)
- Université de Pau, France
-
Allouche, Joachim (författare)
-
visa fler...
-
- Lindgren, Fredrik (författare)
- Uppsala universitet,Strukturkemi
-
- Gorgoi, Mihaela (författare)
- Helmholtz Zentrum Berlin Germany
-
- Rensmo, Håkan (författare)
- Uppsala universitet,Yt- och gränsskiktsvetenskap
-
- Gonbeau, Danielle (författare)
- Université de Pau, France
-
- Edström, Kristina (författare)
- Uppsala universitet,Strukturkemi
-
visa färre...
-
(creator_code:org_t)
- 2012-02-22
- 2012
- Engelska.
-
Ingår i: Chemistry of Materials. - : American Chemical Society (ACS). - 0897-4756 .- 1520-5002. ; 24:6, s. 1107-1115
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Largely based on its very high rechargeable capacity, silicon appears as an ideal candidate for the next generation of negative electrodes for Li-ion batteries. However, a crucial problem with silicon is the large volume expansion undergone upon alloying with lithium, which results in stability problems. Means to avoid such problems are largely linked to the understanding of the interfacial chemistry during charging/discharging. This is especially of great importance when using nanometric silicon particles. In this work, the interfacial mechanisms (reaction of surface oxide, Li-Si alloying process, and passivation layer formation) accompanying lithium insertion/extraction into Si/C/CMC composite electrodes have been scrutinized by Xray photoelectron spectroscopy (XPS). A thorough nondestructive depth-resolved analysis was carried out by using both soft X-rays (100-800 eV) and hard X-rays (2000-7000 eV) from two different synchrotron facilities compared with in-house XPS (1487 eV). The unique combination utilizing hard and soft X-ray photoelectron spectroscopy accompanied with variation of the analysis depth allowed us to access interfacial phase transitions at the surface of silicon particles as well as the composition and thickness of the SEI (electrode/electrolyte interface layer).
Ämnesord
- NATURVETENSKAP -- Kemi -- Oorganisk kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Inorganic Chemistry (hsv//eng)
Nyckelord
- lithium-ion batteries
- silicon
- alloy
- SEI
- XPS
- PES
- synchrotron
- Inorganic chemistry
- Oorganisk kemi
- Kemi med inriktning mot oorganisk kemi
- Chemistry with specialization in Inorganic Chemistry
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas