Emulsion-templated bicontinuous carbon network electrodes for use in 3D microstructured batteries
-
- Asfaw, Habtom Desta (författare)
- Uppsala universitet,Strukturkemi
-
- Roberts, Matthew R. (författare)
- Uppsala universitet,Strukturkemi,St. Andrews
-
- Younesi, Reza (författare)
- Uppsala universitet,Strukturkemi,DTU
-
visa fler...
-
- Edström, Kristina (författare)
- Uppsala universitet,Strukturkemi
-
visa färre...
-
(creator_code:org_t)
- United Kingdom, 2013
- 2013
- Engelska.
-
Ingår i: Journal of Materials Chemistry. - United Kingdom. - 0959-9428 .- 1364-5501. ; 1:44, s. 13750-13758
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- High surface area carbon foams were prepared and characterized for use in 3D structured batteries. Twopotential applications exist for these foams: firstly as an anode and secondly as a current collector supportfor electrode materials. The preparation of the carbon foams by pyrolysis of a high internal phase emulsionpolymer (polyHIPE) resulted in structures with cage sizes of 25 mm and a surface area enhancement pergeometric area of approximately 90 times, close to the optimal configuration for a 3D microstructuredbattery support. The structure was probed using XPS, SEM, BET, XRD and Raman techniques; revealingthat the foams were composed of a disordered carbon with a pore size in the <100 nm range resultingin a BET measured surface area of 433 m2 g-1. A reversible capacity exceeding 3.5 mA h cm2 at acurrent density of 0.37 mA cm-2 was achieved. SEM images of the foams after 50 cycles showed thatthe structure suffered no degradation. Furthermore, the foams were tested as a current collector bydepositing a layer of polyaniline cathode over their surface. High footprint area capacities of500 mA h cm-2 were seen in the voltage range 3.8 to 2.5 V vs. Li and a reasonable rate performancewas observed.
Ämnesord
- NATURVETENSKAP -- Kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences (hsv//eng)
- NATURVETENSKAP -- Kemi -- Materialkemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Materials Chemistry (hsv//eng)
Nyckelord
- Carbon foam
- High internal phase emulsion polymer
- microbattery
- 3D microbattery
- Lithium ion
- Materialvetenskap
- Materials Science
- Chemistry
- Kemi
- Materialvetenskap
- Materials Science