Ion irradiation effects during growth of Mo/V(001) superlattices by dual-target magnetron sputtering
-
- Håkansson, G. (författare)
- Linköping University
-
- Birch, J. (författare)
- Linköping University
-
- Hultman, L. (författare)
- Linköping University
-
visa fler...
-
- Ivanov, I.P. (författare)
- Linköping University
-
- Sundgren, J.E. (författare)
- Linköping University
-
- Wallenberg, LR (författare)
- Lund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH
-
visa färre...
-
(creator_code:org_t)
- 1992
- 1992
- Engelska 14 s.
-
Ingår i: Journal of Crystal Growth. - 0022-0248. ; 121:3, s. 399-412
- Relaterad länk:
-
http://dx.doi.org/10...
-
visa fler...
-
https://lup.lub.lu.s...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Epitaxial (001)-oriented Mo/V superlattice films with wavelengths of ≈ 5 nm have been grown on MgO(001) substrates, kept at 700°C, by dual-target unbalanced magnetron sputter deposition in Ar discharges. Low-energy (15-250 eV) Ar ion irradiation with incident ion-to-metal flux ratio of ≈ 1 during film growth was obtained through the application of a negative potential Vs to the substrate. The effects of ion bombardment on interface roughness and mixing, resputtering rates, and defect structure were investigated using a combination of cross-sectional transmission electron microscopy (XTEM), X-ray diffraction (XRD), and simulation of XRD patterns. High-resolution XTEM images showed that the interfaces were relatively sharp for Vs ≤ 100 V while higher Vs values resulted in more diffuse interfaces indicating ion-induced intermixing. By using a kinematical model of diffraction, and comparing with experimental XRD results, it could be concluded that the intermixing increased from ≈ 0.3 nm (2 monolayers) at Vs = 15 V to & 0.9 nm (6 monolayers) at Vs = 250 V. The inhomogeneous strain showed a large increase for Vs & 50 V. This is explained by an incorporation of point defects. Coherency strain relaxation between layers is suggested to take place through the formation of edge dislocations with Burgers vector 〈110〉 by climb processes. Finally, increasing Vs also resulted in resputtering, preferentially from the V layers.
Ämnesord
- NATURVETENSKAP -- Kemi -- Oorganisk kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Inorganic Chemistry (hsv//eng)
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas