The complex interaction between microstructural features and crack evolution during cyclic testing in heat-treated Al–Si–Mg–Cu cast alloys
-
- Bogdanoff, Toni (författare)
- Jönköping University,JTH, Material och tillverkning
-
- Lattanzi, Lucia (författare)
- Jönköping University,JTH, Material och tillverkning
-
- Merlin, M. (författare)
- Department of Engineering, University of Ferrara, Via Giuseppe Saragat 1, Ferrara, 44122, Italy
-
visa fler...
-
- Ghassemali, Ehsan, 1983- (författare)
- Jönköping University,JTH, Material och tillverkning
-
- Jarfors, Anders E.W. 1963- (författare)
- Jönköping University,JTH, Material och tillverkning
-
- Seifeddine, Salem, 1978- (författare)
- Jönköping University,JTH, Material och tillverkning
-
visa färre...
-
(creator_code:org_t)
- Elsevier, 2021
- 2021
- Engelska.
-
Ingår i: Materials Science & Engineering. - : Elsevier. - 0921-5093 .- 1873-4936. ; 825
- Relaterad länk:
-
https://doi.org/10.1...
-
visa fler...
-
https://doi.org/10.1...
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- The study aimed to investigate crack initiation and propagation at the micro-scale in heat-treated Al–7Si–Mg cast alloys with different copper (Cu) contents. In-situ cyclic testing in a scanning electron microscope coupled with electron back-scattered diffraction and digital image correlation was used to evaluate the complex interaction between the crack path and the microstructural features. The three-nearest-neighbour distance of secondary particles was a new tool to describe the crack propagation in the alloys. The amount of Cu retained in the α-Al matrix after heat treatment increased with the Cu content in the alloy and enhanced the strength with a slight decrease in elongation. During cyclic testing, the two-dimensional (2D) crack path appeared with a mixed propagation, both trans- and inter-granular, regardless of the Cu content of the alloy. On fracture surfaces, multiple crack initiation points were detected along the thickness of the samples. The debonding of silicon (Si) particles took place during crack propagation in the Cu-free alloy, while cracking of Si particles and intermetallic phases occurred in the alloy with 3.2 wt% Cu. Three-dimensional tomography using focused ion beam revealed that the improved strength of the α-Al matrix changes the number of cracked particles ahead of the propagating crack with Cu concentration above 1.5 wt%.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
Nyckelord
- Aluminium alloys
- Casting methods
- Characterisation
- Electron microscopy
- Fatigue
- After-heat treatment
- Aluminum alloys
- Copper alloys
- Crack initiation
- Crack propagation
- Cracks
- Fatigue testing
- Ion beams
- Magnesium alloys
- Scanning electron microscopy
- Cast alloys
- Casting method
- Characterization
- Crack paths
- Cracks propagation
- Cu content
- Cyclic testing
- matrix
- Microstructural features
- Silicon particles
- Fatigue of materials