- Sadeghimeresht, Esmaeil,1985-Högskolan Väst,Avdelningen för avverkande och additativa tillverkningsprocesser (AAT),PTW (författare)
Ni-based coatings for high temperature corrosion protection
- BokEngelska2018
Förlag, utgivningsår, omfång ...
- Trollhättan :University West,2018
- 78 s.
- electronicrdacarrier
Nummerbeteckningar
- LIBRIS-ID:oai:DiVA.org:hv-12277
- ISBN:9789187531705
- ISBN:9789187531699
- https://urn.kb.se/resolve?urn=urn:nbn:se:hv:diva-12277URI
Kompletterande språkuppgifter
- Språk:engelska
- Sammanfattning på:engelska
Ingår i deldatabas
- SwePubSwePub
Klassifikation
Serie
- PhD Thesis ;23
Anmärkningar
- Biomass/waste-fired boilers severely suffer from high temperature corrosion of critical load-bearing components, e.g. water-wall and superheater tubes, due to presence of Cl-containing corrosive species. Deposition of a dense and adherent Ni-based coating by high velocity air-fuel (HVAF) thermal spray technique is a promising approach to extend the component's lifetime and, hence, increase the thermal/electrical efficiency of the boilers. In this research, high temperature corrosion of candidate Ni-based coatings –Ni21Cr, Ni21Cr7AlY, Ni5Al, Ni21Cr9Mo, Ni21Cr9Mo-SiO2 – sprayed by HVAF has been investigated through detailed laboratory studies in ambient air, moisture and HCl-laden environments. The exposures were conducted at 600 °C for up to 168 h with and without presence of KCl salt. All coatings were highly protective in all environments in the absence of KCl due to formation of corresponding protective scales of alumina or chromia on the coating surface. When KCl was introduced, chromia-forming coatings degraded through a two-stage mechanism; 1) formation of K2CrO4 and Cl- followed by diffusion of Cl- through oxide grain boundaries, leading to formation of Cl2, metal chlorides as well as a nonprotective oxide, and 2) inward diffusion of the formed Cl2 through defects in the non-protective oxide, leading to metal chloride evaporation and breakaway oxidation. The corrosion behavior of the chromia-forming Ni21Cr coating was improved by addition of alloying elements such as Al and Mo. It was also shown that adding dispersed SiO2 further increased the corrosion resistance of the coatings. The oxide scale formed in the presence of SiO2 effectively suppressed Cl- ingress and lowered the corrosion rate, since the formed oxide was continuous, adherent andrich in Cr. The performance of the coatings in the complex Cl-containing environment was ranked as (from highest to lowest corrosion resistance); Ni21Cr9Mo-SiO2 > Ni21Cr7AlY > Ni5Al > Ni21Cr9Mo > Ni21Cr, confirming the enhanced corrosion protection of chromia-forming coatings in the presence of alloying elements and dispersed SiO2.
Ämnesord och genrebeteckningar
- TEKNIK OCH TEKNOLOGIER Materialteknik Bearbetnings-, yt- och fogningsteknik hsv//swe
- ENGINEERING AND TECHNOLOGY Materials Engineering Manufacturing, Surface and Joining Technology hsv//eng
- Thermal Spray Coating; HVAF; High Temperature Corrosion Protection; Composition; Microstructure; Dispersed Oxide
- Production Technology
- Produktionsteknik
- Manufacturing and materials engineering
- Produktions- och materialteknik
Biuppslag (personer, institutioner, konferenser, titlar ...)
- Joshi, Shrikant V.,1960-Högskolan Väst,Avdelningen för avverkande och additativa tillverkningsprocesser (AAT)(Swepub:hv)shrjos (preses)
- Markocsan, Nicolaie,1967-Högskolan Väst,Avdelningen för avverkande och additativa tillverkningsprocesser (AAT)(Swepub:hv)tnm (preses)
- Vuoristo, PetriTampere University, Tampere, Finland (opponent)
- Högskolan VästAvdelningen för avverkande och additativa tillverkningsprocesser (AAT) (creator_code:org_t)
Internetlänk
Hitta via bibliotek
- Ni-based coatings for high temperature corrosion protection (Sök publikationen i LIBRIS)
Till lärosätets databas
- 1 av 1
- Föregående post
- Nästa post
- Till träfflistan
Hitta mer i SwePub
- Av författaren/redakt...
- Sadeghimeresht, ...
- Joshi, Shrikant ...
- Markocsan, Nicol ...
- Vuoristo, Petri
- Om ämnet
-
- TEKNIK OCH TEKNOLOGIER
- TEKNIK OCH TEKNO ...
- och Materialteknik
- och Bearbetnings yt ...
- Delar i serien
- PhD Thesis ;
- Av lärosätet
- Högskolan Väst
Sök utanför SwePub
- Sök vidare i:
- Google Book Search
- Google Scholar
Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.
- Copyright © LIBRIS - Nationella bibliotekssystem
- LIBRIS.kb.se