Effect of Powder Recycling on the Fracture Behavior of Electron Beam Melted Alloy 718
-
- Gruber, Hans, 1983 (author)
- Chalmers University of Technology, Department of Industrial and Materials Science, Division of Materials and Manufacture, Gothenburg, SE-412 96, Sweden,Chalmers tekniska högskola
-
- Karimi Neghlani, Paria, 1986- (author)
- Högskolan Väst,Avdelningen för avverkande och additativa tillverkningsprocesser (AAT),PTW,University West
-
- Hryha, Eduard, 1980 (author)
- Chalmers University of Technology, Department of Industrial and Materials Science, Division of Materials and Manufacture, Gothenburg, SE-412 96, Sweden,Chalmers tekniska högskola
-
show more...
-
- Nyborg, Lars, 1958 (author)
- Chalmers University of Technology, Department of Industrial and Materials Science, Division of Materials and Manufacture, Gothenburg, SE-412 96, Sweden,Chalmers tekniska högskola
-
show less...
-
(creator_code:org_t)
- 2018-07-25
- 2018
- English.
-
In: Powder Metallurgy Progress. - : de Gruyter. - 1335-8987 .- 1339-4533. ; 18:1, s. 40-48
- Related links:
-
https://doi.org/10.1...
-
show more...
-
https://content.scie...
-
https://research.cha... (primary) (free)
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
https://research.cha...
-
show less...
Abstract
Subject headings
Close
- Understanding the effect of powder feedstock alterations during multicycle additive manufacturing on the quality of built components is crucial to meet the requirements on critical parts for aerospace engine applications. In this study, powder recycling of Alloy 718 during electron beam melting was studied to understand its influence on fracture behavior of Charpy impact test bars. High resolution scanning electron microscopy was employed for fracture surface analysis on test bars produced from virgin and recycled powder. For all investigated samples, an intergranular type of fracture, initiated by non-metallic phases and bonding defects, was typically observed in the regions close to or within the contour zone. The fracture mode in the bulk of the samples was mainly moderately ductile dimple fracture. The results show a clear correlation between powder degradation during multi-cycle powder reuse and the amount of damage relevant defects observed on the fracture surfaces. In particular, samples produced from recycled powder show a significant amount of aluminum-rich oxide defects, originating from aluminum-rich oxide particulates on the surface of the recycled powder. © 2018 H. Gruber et al., published by Sciendo.
Subject headings
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Annan materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Other Materials Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Keyword
- additive manufacturing of Alloy 718
- electron beam melting
- powder recycling
- powder degradation
- fractography of AM components
- Manufacturing and materials engineering
- Produktions- och materialteknik
- Production Technology
- Produktionsteknik
Publication and Content Type
- vet (subject category)
- art (subject category)
Find in a library
To the university's database