Oxidation behaviour of HVAF-sprayed NiCr coating in moisture-laden environment

Sadeghimeresht, Esmaeil,1985-Högskolan Väst,Avdelningen för avverkande och additativa tillverkningsprocesser (AAT),PTW,University West (författare)

Reducing CO2 emissions from power generation plants is intimately related to enhancing their thermal efficiency, which can be achieved by increasing the temperature/pressure of steam. However, any increase in steam temperature is inevitably accompanied by accelerated oxidation of boiler components. The use of renewable fuels such as biomass increases the problem by introducing a number of corrosive compounds into the boiler environment, resulting in more rapid degradation of components. Although thermal sprayed coatings are techno-commercially attractive solutions for augmenting the durability of degradation-prone boiler components and are already used, further improvements in their performance are continuously sought. High-velocity air fuel (HVAF) coatings are promising in this context. In the present work, isothermal oxidation behavior of a candidate HVAF-sprayed Ni21Cr was studied in N2 + 5% O2 + 20% H2O at 600°C for 168h. The oxide scale growth mechanisms were studied by BIB/SEM/EDX to evaluate the effectiveness of the coatings. It was found that the water vapor effect is insignificant due to the Cr reservoir in the Ni21Cr coating, which yielded enhanced oxidation protection by forming nano-scale Cr2O3.

TEKNIK OCH TEKNOLOGIER Materialteknik Bearbetnings-, yt- och fogningsteknik hsv//swe
ENGINEERING AND TECHNOLOGY Materials Engineering Manufacturing, Surface and Joining Technology hsv//eng
TEKNIK OCH TEKNOLOGIER Maskinteknik Energiteknik hsv//swe
ENGINEERING AND TECHNOLOGY Mechanical Engineering Energy Engineering hsv//eng
TEKNIK OCH TEKNOLOGIER Kemiteknik Korrosionsteknik hsv//swe
ENGINEERING AND TECHNOLOGY Chemical Engineering Corrosion Engineering hsv//eng
Air
Binary alloys
Boiler corrosion
Boilers
Nanotechnology
Oxidation
Reservoirs (water)
Scale (deposits)
Accelerated oxidations
Attractive solutions
High velocity air fuels
Isothermal oxidations
Oxidation protection
Power generation plants
Reducing co2 emissions
Thermal sprayed coating
Sprayed coatings
Manufacturing and materials engineering
Produktions- och materialteknik
Production Technology
Produktionsteknik

Eklund, Johan,1991Chalmers University of Technology, Department of Environmental Inorganic Chemistry, Gothenburg, 412 96, Sweden,Chalmers tekniska högskola(Swepub:cth)johekl (författare)
Phother Simon, Julien,1991Chalmers University of Technology, Department of Environmental Inorganic Chemistry, Gothenburg, 412 96, Sweden,Chalmers tekniska högskola(Swepub:cth)photer (författare)
Lyske, J.Chalmers University of Technology, Department of Environmental Inorganic Chemistry, Gothenburg, 412 96, Sweden,Chalmers tekniska högskola (författare)
Markocsan, Nicolaie,1967-Högskolan Väst,Avdelningen för avverkande och additativa tillverkningsprocesser (AAT),PTW,University West(Swepub:hv)tnm (författare)
Joshi, Shrikant V.,1960-Högskolan Väst,Forskningsmiljön produktionsteknik(PTW),PTW,University West(Swepub:hv)shrjos (författare)
Högskolan VästAvdelningen för avverkande och additativa tillverkningsprocesser (AAT) (creator_code:org_t)

Ingår i:Proceedings of the International Thermal Spray Conference & Exposition (ITSC 2017)New York : Curran Associates, Inc.2, s. 644-6469781510858220
Ingår i:Proceedings of the International Thermal Spray ConferenceNew York : Curran Associates, Inc.2, s. 644-646

Av författaren/redakt...: Sadeghimeresht, ...; Eklund, Johan, 1 ...; Phother Simon, J ...; Lyske, J.; Markocsan, Nicol ...; Joshi, Shrikant ...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Bearbetnings yt ...

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Maskinteknik; och Energiteknik

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Kemiteknik; och Korrosionsteknik

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.