Response of different electron beam melting produced Alloy 718 microstructures to thermal post-treatments
- Artikel/kapitelEngelska2020
Förlag, utgivningsår, omfång ...
-
Elsevier BV,2020
-
printrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:hv-15744
-
https://urn.kb.se/resolve?urn=urn:nbn:se:hv:diva-15744URI
-
https://doi.org/10.1016/j.matchar.2020.110498DOI
-
https://research.chalmers.se/publication/518108URI
-
https://research.chalmers.se/publication/517982URI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
Electron beam melting (EBM) was used to produce Alloy 718 specimens with different microstructures (columnar, equiaxed and a combination thereof) by varying the process parameters. The present study aimed at assessing the response of such varying as-built microstructures to identical thermal post-treatments, which included hot isostatic pressing (HIPing) followed by heat treatment involving solution treatment and aging. The effect of these treatments on defect content, grain structure, hardness and phase constitution in the specimens was specifically analysed. Despite differences in defect content of as-built specimens with distinct microstructures, HIPing was effective in closing defects leading to samples exhibiting similar density. After HIPing, grains with equiaxed morphology or columnar grains with lower aspect ratio showed higher tendency for grain growth in comparison to the columnar grains with higher aspect ratio. The various factors affecting the stability of grains during HIPing of builds with distinct microstructures were investigated. These factors include texture, grain size, and secondary phase particles. The carbide sizes in the different as-built samples varied but were found to be largely unaffected by the post-treatments. Solution treatment following HIPing led to greater precipitation of grain boundary ÎŽ phase in regions with coarser grains than the smaller ones. After HIPing and heat treatment, all specimens exhibited similar precipitation of γⳠphase regardless of their grain morphology in the as-built condition. © 2020 The Author(s)
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Goel, Sneha,1993-Högskolan Väst,Avdelningen för avverkande och additativa tillverkningsprocesser (AAT),PTW,University West(Swepub:hv)sngo0001
(författare)
-
Klement, Uta,1962Chalmers University of Technology, Department of Industrial and Material Science, Gothenburg, 41296, Sweden,Chalmers tekniska högskola(Swepub:cth)uk
(författare)
-
Joshi, Shrikant V.,1960-Högskolan Väst,Forskningsmiljön produktionsteknik(PTW),PTW,University West(Swepub:hv)shrjos
(författare)
-
Högskolan VästAvdelningen för avverkande och additativa tillverkningsprocesser (AAT)
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Materials Characterization: Elsevier BV1671044-58031873-4189
Internetlänk
Hitta via bibliotek
Till lärosätets databas