The Effect of Grain Size on theSusceptibility Towards Strain Age Crackingof Wrought Haynes® 282®

• The effect of grain size on the suceptibility towards strain age cracking (SAC) has been investigated for Haynes® 282® in the tempeature range of 750 to 950°C after isothermal exposure up to 1800s. Grain growth was induced by heattreating the material at 1150°C for 2h, resulting in a fourfold increase in grain size. Hardness was significanlty reduced after heat treatment as compared to millannealed material. Large grain size resulted in intergranular fracture over a widertemperature range than small grain size material. Ductility was lowest at 850°C, while lower values were observed to be correlated to increased grain size. The rapid formation of grain boundary carbide networks in Haynes® 282® is found to be notable to compensate for higher local stresses on grain boundaries due to incresedgrain size. 

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Keramteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Ceramics (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Annan materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Other Materials Engineering (hsv//eng)

Nyckelord

. Welding

Nickel based superalloy

Weld cracking

Strain age cracking

Haynes® 282®

Gleeble

Production Technology

Produktionsteknik

Publikations- och innehållstyp

vet (ämneskategori)

kon (ämneskategori)