High velocity air fuel (HVAF) spraying of nickel phosphorus-coated cubic-boron nitride powders for realizing high-performance tribological coatings
- Artikel/kapitelEngelska2022
Förlag, utgivningsår, omfång ...
-
Elsevier Editora Ltda,2022
-
electronicrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:hv-18290
-
https://urn.kb.se/resolve?urn=urn:nbn:se:hv:diva-18290URI
-
https://doi.org/10.1016/j.jmrt.2022.02.058DOI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
The authors thank NUCoP project (Energimyndigheten, Sweden, Dnr. 2018e003191, Project nr. P46393-1 and the knowledge foundation, Sweden, for its financial support to projectHiPerCOAT (Dnr. 20180197) for their financial support. Theauthors also thank Mr. Magnus Sandberg, University West, forassisting in spraying the coatings and Mr. Mats Hogstr € om, €University West, for performing heat treatment.
-
High velocity air fuel (HVAF) spraying is an emergent thermal spray process, which is used in this work to realize high-performance large area tribological coatings of nickel-phosphorus cladded cubic-boron nitride (c-BN) particles. To the best of authorsâ knowledge, this is the first time that HVAF has been utilized for developing NiâP coatings reinforced with c-BN (NBN). The importance of appropriate processing was highlighted by utilizing two different nozzle configurations, for which microstructure, phase analysis and hardness results demonstrates considerable differences. Furthermore, the coatings were subjected to sliding wear tests to assess their friction and wear characteristics. Post-wear SEM analysis reveals the associated wear mechanisms. Effect of annealing on tribological performance of NBN coatings was also examined, and it is shown that optimal processing can preclude the need for post-treatment. Results ensuing from this work lay the foundation for new generation of HVAF-sprayed wear resistant metal/c-BN composite coatings for diverse applications. © 2022 The Author(s)
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Rossetti, MatteoHögskolan Väst,Institutionen för ingenjörsvetenskap,Universita di Modena e Reggio Emilia, Via Pietro Vivarelli 10/1, 41125 Modena (ITA),PTW
(författare)
-
Björklund, Stefan,1969-Högskolan Väst,Avdelningen för avverkande och additativa tillverkningsprocesser (AAT),PTW(Swepub:hv)tsb
(författare)
-
Sowers, SusanneHyperion Materials & Technologies, 43085 Worthington, Ohio (USA)
(författare)
-
Dumm, TimothyHyperion Materials & Technologies, 43085 Worthington, Ohio (USA)
(författare)
-
Kim, ChungHyperion Materials & Technologies, 43085 Worthington, Ohio (USA)
(författare)
-
Joshi, Shrikant V.,1960-Högskolan Väst,Avdelningen för avverkande och additativa tillverkningsprocesser (AAT),PTW(Swepub:hv)shrjos
(författare)
-
Högskolan VästAvdelningen för avverkande och additativa tillverkningsprocesser (AAT)
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Journal of Materials Research and Technology: Elsevier Editora Ltda18, s. 59-742238-78542214-0697
Internetlänk
Hitta via bibliotek
Till lärosätets databas