Effect of Austenitization and Tempering on the Microstructure and Mechanical Properties of a 5 wt% Cr Cold Work Tool Steel

Rehan, ArbabHögskolan Väst,Forskningsmiljön produktionsteknik(PTW),Uddeholms AB, Hagfors, Sweden,PTW (författare)

The effects of austenitization and tempering temperatures for a 5 wt% Cr cold work tool steel are studied with an aim of understanding the influence on microstructure and mechanical properties. Microstructures are characterized with scanning electron microscopy and light optical microscopy. Retained austenite contents and martensite start temperatures are measured by X-ray diffraction and dilatometry, respectively. Hardness, impact toughness, and compressive yield strength are also determined. When the austenitization temperature is increased from 1020 or 1050 to 1075 °C, followed by tempering at 525 °C, significant hardness is gained while there is no increase in compressive yield strength. Higher austenitization temperatures also produce larger amounts of retained austenite. At the same time, the impact toughness is reduced due to coarsening of the martensitic microstructure. When the steel is tempered at 200 °C, a higher impact toughness and a higher volume fraction of retained austenite are observed. Retained austenite is not found after tempering at temperatures of 525 °C or above. It is concluded that the best combination of mechanical properties is achieved by austenitization at 1020 or 1050 °C followed by tempering at 525 °C.

TEKNIK OCH TEKNOLOGIER Materialteknik Bearbetnings-, yt- och fogningsteknik hsv//swe
ENGINEERING AND TECHNOLOGY Materials Engineering Manufacturing, Surface and Joining Technology hsv//eng
Cold work
tool steel
austenitization
tempering
retained austenite
impact toughness
Production Technology
Produktionsteknik
Manufacturing and materials engineering
Produktions- och materialteknik

Medvedeva, AnnaUddeholms AB, Hagfors, Sweden (författare)
Högman, BerneUddeholms AB, Hagfors, Sweden (författare)
Svensson, Lars-Erik,1951-Högskolan Väst,Avdelningen för svetsteknologi (SV),Welding group, PTW(Swepub:hv)larsve (författare)
Karlsson, Leif,1952-Högskolan Väst,Avdelningen för svetsteknologi (SV),PTW(Swepub:hv)leikar (författare)
Högskolan VästForskningsmiljön produktionsteknik(PTW) (creator_code:org_t)

Ingår i:Steel Research International: Wiley12:1 December, s. 1609-16181611-36831869-344X

Av författaren/redakt...: Rehan, Arbab; Medvedeva, Anna; Högman, Berne; Svensson, Lars-E ...; Karlsson, Leif, ...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Bearbetnings yt ...

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.