Crystallization of Metal Fluoride Hydrates from Mixed Acid Solutions

• In this work crystal growth and nucleation of b-FeF3×3H2O and crystallization of chromium (III), iron (III) and nickel (II) fluoride hydrates from mixed acid (1-3 mol/kg HNO3 and 1-6 mol/kg free HF) have been investigated. The solubility of b-FeF3×3H2O has been determined in solutions of different hydrofluoric acid (1-7mol/ kg) and nitric acid (0-7mol/ kg) concentrations at 30, 40 and 50°C. The total iron concentration at equilibrium ranges from about 1 to 35 g/kg solution. In the range of investigated conditions the solubility in terms of total iron content increases with increasing temperature and decreases with increasing concentration of hydrofluoric acid and nitric acid. The results are analysed by examining the chemical speciation in the solutions. The crystal growth kinetics of b-FeF3×3H2O crystals have been studied by performing seeded isothermal desupersaturation experiments in solutions of 1.5-3.0 mol/ kg nitric acid and 1.4- 5.6 mol/ kg free hydrofluoric acid at 30, 40 and 50°C. The results show that the crystal growth is surface integration controlled. When the driving force is based on a proper speciation no clear correlation of the growth rate with hydrofluoric acid or nitric acid concentration is found. The rate is about the same in industrial pickle liquor as in pure acid solutions. The growth rate at a supersaturation ratio (c(FeF3)free/cs(FeF3)free) of 2 was found to be 5.2×10-12m/s at 30°C, 7.9×10-12m/s at 40°C and 20×10-12m/s at 50°C. Thus, the crystal growth rate at 50°C is about four times higher than at 30°C. The temperature dependence of the rate constant corresponds to an activation energy of 55kJ/ mol. Crystallization from solutions supersaturated with both Cr(III) and Fe(III) has been investigated and it has been observed that Fe(III) and Cr(III) crystallizes in the form of Cr(Fe)F3×3H2O which is isostructural with CrF3×3H2O. Iron(III) and nickel(II) crystallizes into an unidentified fluoride hydrate crystal. The crystal growth rate of CrF3×3H2O at 50°C is about the same as the growth rate of b-FeF3×3H2O crystals.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Kemiteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Chemical Engineering (hsv//eng)

Nyckelord

crystallization

crystal growth

b-FeF3.3H2O

iron fluoride trihydrate

CrF3.3H2O

pickling

pickle bath

hydrofluoric acid

nitric acid

stainless steel

Chemical engineering

Kemiteknik

Publikations- och innehållstyp

vet (ämneskategori)

dok (ämneskategori)