Investigating the effectof slag on decarburization in an AOD converter using a fundamental model

QC 20130222
A high-temperature thermodynamics model has been coupled with a fundamental mathematical model describing the fluid flow, where boundary conditions were chosen based on data for an industrial AOD converter. Using this model, the effect of both slag phases (a liquid part and a solid part) on the decarburization was studied. More specifically, the separation of chromium oxide to liquid slag as well as the effect of the amount of rigid top slag (solid)on the decarburization was investigated. The liquid slag was considered with respect to the uptake of chromium oxide, while the rigid top slag was only considered with respect to the increase of the metallostatic pressure in the steel melt. The results suggest that separation of chromium oxide to liquid slag results in a decreased decarburization rate. The same conclusion can be drawn with respect to the amount of solid top slag.

Tilliander, AndersKTH,Tillämpad processmetallurgi(Swepub:kth)u1zaf6ay (författare)
Jonsson, Lage,1949-KTH,Tillämpad processmetallurgi(Swepub:kth)u18isdqo (författare)
Jönsson, PärKTH,Tillämpad processmetallurgi(Swepub:kth)u118w09b (författare)
KTHTillämpad processmetallurgi (creator_code:org_t)

Av författaren/redakt...: Andersson, Nils; Tilliander, Ande ...; Jonsson, Lage, 1 ...; Jönsson, Pär

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Metallurgi och m ...

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.