Transparent Nanocellulosic Multilayer Thin Films on Polylactic Acid with Tunable Gas Barrier Properties

↓ Direkt till sidans innehåll
↓ Direkt till sidans sekundära innehåll (sidomenyn)

Sökning: WFRF:(Aulin Christian) > Transparent Nanocel...

Aulin, ChristianRISE,KTH,Fiber- och polymerteknologi,Wallenberg Wood Science Center,Innventia,KTH Royal Institute of Technology, Sweden (författare)

Transparent Nanocellulosic Multilayer Thin Films on Polylactic Acid with Tunable Gas Barrier Properties

Artikel/kapitelEngelska2013

Förlag, utgivningsår, omfång ...

2013-07-22
American Chemical Society (ACS),2013
printrdacarrier

Nummerbeteckningar

LIBRIS-ID:oai:DiVA.org:kth-128474
https://urn.kb.se/resolve?urn=urn:nbn:se:kth:diva-128474URI
https://doi.org/10.1021/am401700nDOI
https://urn.kb.se/resolve?urn=urn:nbn:se:ri:diva-9775URI

Kompletterande språkuppgifter

Språk:engelska
Sammanfattning på:engelska

Ingår i deldatabas

SwePubSwePub

Klassifikation

Ämneskategori:ref swepub-contenttype
Ämneskategori:art swepub-publicationtype

Anmärkningar

QC 20130912
The layer-by-layer (LbL) deposition method was used for the build-up of alternating layers of nanofibrillated cellulose (NFC) or carboxymethyl cellulose (CMC) with a branched, cationic polyelectrolyte, polyethyleneimine (PEI) on flexible poly (lactic acid) (PLA) substrates. With this procedure, optically transparent nanocellulosic films with tunable gas barrier properties were formed. 50 layer pairs of PEI/NFC and PEI/CMC deposited on PLA have oxygen permeabilities of 0.34 and 0.71 cm(3).mu m/m(2).day.kPa at 23 degrees C and 50% relative humidity, respectively, which is in the same range as polyvinyl alcohol and ethylene vinyl alcohol. The oxygen permeability of these multilayer nanocomposites outperforms those of pure NFC films prepared by solvent-casting. The nanocellulosic LbL assemblies on PLA substrates was in detailed characterized using a quartz crystal microbalance with dissipation (QCM-D). Atomic force microscopy (AFM) reveals large structural differences between the PEI/NFC and the PEI/CMC assemblies, with the PEI/NFC assembly showing a highly entangled network of nanofibrils, whereas the PEI/CMC surfaces lacked structural features. Scanning electron microscopy images showed a nearly perfect uniformity of the nanocellulosic coatings on PLA, and light transmittance results revealed remarkable transparency of the LbL-coated PLA films. The present work demonstrates the first ever LbL films based on high aspect ratio, water-dispersible nanofibrillated cellulose, and water-soluble carboxymethyl cellulose polymers that can be used as multifunctional films and coatings with tailorable properties, such as gas barriers and transparency. Owing to its flexibility, transparency and high-performance gas barrier properties, these thin film assemblies are promising candidates for several large-scale applications, including flexible electronics and renewable packaging.

Ämnesord och genrebeteckningar

TEKNIK OCH TEKNOLOGIER Nanoteknik hsv//swe
ENGINEERING AND TECHNOLOGY Nano-technology hsv//eng
NATURVETENSKAP Kemi Annan kemi hsv//swe
NATURAL SCIENCES Chemical Sciences Other Chemistry Topics hsv//eng
TEKNIK OCH TEKNOLOGIER Materialteknik Annan materialteknik hsv//swe
ENGINEERING AND TECHNOLOGY Materials Engineering Other Materials Engineering hsv//eng
nanocellulose
oxygen permeability
water vapor permeability
multilayer
transparency
gas barrier

Biuppslag (personer, institutioner, konferenser, titlar ...)

Karabulut, ErdemKTH,Fiber- och polymerteknologi,KTH Royal Institute of Technology, Sweden(Swepub:kth)u1cuu1bi (författare)
Tran, AmyKTH,Fiber- och polymerteknologi,KTH Royal Institute of Technology, Sweden(Swepub:kth)u1kxmw6r (författare)
Wågberg, LarsKTH,Fiber- och polymerteknologi,Wallenberg Wood Science Center,KTH Royal Institute of Technology, Sweden(Swepub:kth)u14jbte3 (författare)
Lindström, TomRISE,KTH,Wallenberg Wood Science Center,Innventia,KTH Royal Institute of Technology, Sweden(Swepub:kth)u1pt0ti8 (författare)
KTHFiber- och polymerteknologi (creator_code:org_t)

Sammanhörande titlar

Ingår i:ACS Applied Materials and Interfaces: American Chemical Society (ACS)5:15, s. 7352-73591944-82441944-8252

Internetlänk

Hitta via bibliotek

ACS Applied Materials and Interfaces (Sök värdpublikationen i LIBRIS)

Till lärosätets databas

Hitta mer i SwePub

Av författaren/redakt...: Aulin, Christian; Karabulut, Erdem; Tran, Amy; Wågberg, Lars; Lindström, Tom

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Nanoteknik

NATURVETENSKAP: NATURVETENSKAP; och Kemi; och Annan kemi

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Annan materialte ...

Artiklar i publikationen: ACS Applied Mate ...

Av lärosätet: Kungliga Tekniska Högskolan; RISE

Sök utanför SwePub

Sök vidare i:: Google; Google Book Search; Google Scholar

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

LIBRIS.kb.se