Wettability of Al2O3, MgO and Ti2O3 by Liquid Iron and Steel
- Artikel/kapitelEngelska2015
Förlag, utgivningsår, omfång ...
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:kth-175952
-
https://urn.kb.se/resolve?urn=urn:nbn:se:kth:diva-175952URI
-
https://doi.org/10.2355/isijinternational.ISIJINT-2014-820DOI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
QC 20151102
-
The wetting behavior of liquid iron and steel on Al2O3, MgO and Ti2O3 substrates was measured by using the sessile drop method. Measurements were carried out using a controlled oxygen partial pressure and using an argon protected atmosphere. For the Al2O3 and MgO substrates, reaction layers in form of FeAl2O4 and MgO-FeO (solid solution) were formed. These layers slightly decreased the contact angle and surface tension values after a full melting. For a Ti2O3 substrate in contact with pure Fe, no-reaction could be observed at the interface. Furthermore, the contact angle and surface tension values were almost stable after a full melting. For a Ti2O3 substrate in contact with steel, the contact angle and surface tension values decreased steeply after a full melting, due to the formation Al2TiO5 reaction layer formation at the interface.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Shibata, Hiroyuki
(författare)
-
Sukenaga, Sohei
(författare)
-
Jönsson, Pär GöranKTH,Tillämpad processmetallurgi(Swepub:kth)u118w09b
(författare)
-
Nakajima, KeijiKTH,Tillämpad processmetallurgi(Swepub:kth)u1kahymd
(författare)
-
KTHTillämpad processmetallurgi
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:ISIJ International55:9, s. 1882-18900915-15591347-5460
Internetlänk
Hitta via bibliotek
Till lärosätets databas