CTAB-Assisted Hydrothermal Synthesis and Magnetic Characterization of NixCo1-xFe2O4 Nanoparticles (x=0.0, 0.6, 1.0)

• Nickel ferrite, NixCo1-xFe2O4, NPs (where x = 0.0, 0.6 and 1.0) were successfully synthesized by a rapid and reproducible CTAB-assisted hydrothermal route. The influence of different hydrolyzing agents on the particle size and magnetic behavior of NixCo1-xFe2O4 NPs was investigated. Particles showed very high phase purity and crystallinity in powder XRD analysis. Compositions of Co, Fe, and Ni in fabricated powders were also determined by AAS and results are in very good agreement with the targeted compositions. Samples hydrolyzed using NH3 showed no significant changes in the particle size and morphology. NH3 hydrolyzed samples were much smaller than their NaOH hydrolyzed counterparts, which was attributed to the strength and concentration of the hydrolyzing agents, NH3 being about 6 times more concentrated than NaOH. This in turn influenced the nucleation rate thus the size of each nucleus formed. Strong temperature and Ni concentration dependence of magnetic parameters was observed. These samples are considered as promising materials for high density magnetic recording media.

Nyckelord

Magnetic materials

Spinels

XRD

Coercivity

Hydrothermal synthesis

ferrite nanocrystallites

combustion synthesis

spinel ferrites

nickel

route

cobalt

cofe2o4

nife2o4

copper

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)