Solar-blind 4.55 eV band gap Mg0.55Zn0.45O components fabricated using quasi-homo buffers

QC 20100525
A route for synthesizing high Mg content single-phase wurtzite MgZnO films having band gaps in the solar-blind region is demonstrated by employing molecular beam epitaxy on Al2O3 substrates. Importantly, a low Mg content "quasi-homo" buffer, Mg0.17Zn0.83O, was applied to accommodate a host of structural discrepancies and therefore, avoiding phase separation in a high Mg content film, Mg0.55Zn0.45O, as proved by X-ray diffraction. The Mg fraction in the overgrown single-phase epilayer, Mg0.55Zn0.45O, was confirmed by Rutherford backscattering spectrometry.

Mei, Z. X. (författare)
Zhang, T. C. (författare)
Liu, Y. P. (författare)
Guo, Y. (författare)
Du, X. L. (författare)
Hallén, Anders.KTH,Mikroelektronik och Informationsteknik, IMIT(Swepub:kth)u11ywmz1 (författare)
Zhu, J. J. (författare)
Kuznetsov, A. Yu (författare)
KTHMikroelektronik och Informationsteknik, IMIT (creator_code:org_t)

Ingår i:Journal of Crystal Growth: Elsevier BV311:18, s. 4356-43590022-02481873-5002

Av författaren/redakt...: Liu, Z. L.; Mei, Z. X.; Zhang, T. C.; Liu, Y. P.; Guo, Y.; Du, X. L.; visa fler...; Hallén, Anders.; Zhu, J. J.; Kuznetsov, A. Yu; visa färre...

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.