Investigation of damage behaviour and isolation effect of n-type 6H-SiC by implantation of oxygen
-
Wang, L. W. (författare)
-
Huang, J. P. (författare)
-
Duo, X. Z. (författare)
-
visa fler...
-
Song, Z. T. (författare)
-
Lin, C. L. (författare)
-
- Zetterling, Carl-Mikael (författare)
- KTH,Mikroelektronik och informationsteknik, IMIT
-
- Östling, Mikael (författare)
- KTH,Mikroelektronik och informationsteknik, IMIT
-
visa färre...
-
(creator_code:org_t)
- 2000-05-31
- 2000
- Engelska.
-
Ingår i: Journal of Physics D. - : IOP Publishing. - 0022-3727 .- 1361-6463. ; 33:12, s. 1551-1555
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Silicon carbide is an important wide-band-gap semiconductor for high temperature, high-voltage, high-power and high-frequency devices. Electrical isolation is an important aspect for device applications. In this report, oxygen ions, 70 keV with doses ranging from 5 x 10(13) to 5 x 10(15) cm(-2), have been implanted into n-type 6H-SiC to investigate the possibility of forming a high-resistive layer. The damage behaviour and internal stress were checked by Rutherford backscattering spectroscopy and channelling, and an x-ray rocking curve, respectively. Atomic force microscope observations revealed that the surface morphology is quite sensitive to the implantation even at a dose of 1 x 10(14) cm(-2) After annealing in nitrogen at 1200 degrees C, no remarkable damage recovery could be seen if the deposit damage energy is over the critical value. Schottky structures of Au/SiC have been fabricated on the annealed samples and I-V curves of metal/SiC/InGeNi were measured at room temperature at both forward and reverse bias; the electrical isolation effect was observed at proper implantation dosages. The results indicated that there exists a dose window for electrical isolation.
Nyckelord
- enhanced thermal-oxidation
- ion-implantation
- silicon-carbide
- amorphization
- layers
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas