On flux effects in a low alloy steel from a Swedish reactor pressure vessel

• This study aims to investigate the presence of Unstable Matrix Defects in irradiated pressure vessel steel from weldments of the Swedish PWR Ringhals 4 (R4). Hardness tests have been performed on low flux (surveillance material) and high flux (Halden reactor) irradiated material samples in combination with heat treatments at temperatures of 330, 360 and 390 °C in order to reveal eventual recovery of any hardening features induced by irradiation. The experiments carried out in this study could not reveal any hardness recovery related to Unstable Matrix Defects at relevant temperatures. However, a difference in hardness recovery was found between the low and the high flux samples at heat treatments at higher temperatures than expected for the annihilation of Unstable Matrix Defects–the observed recovery is here attributed to differences of the solute clusters formed by the high and low flux irradiations.

Subject headings

NATURVETENSKAP  -- Fysik (hsv//swe)

NATURAL SCIENCES  -- Physical Sciences (hsv//eng)

Keyword

Defects

Hardness

Heat treatment

High strength steel

Irradiation

Pressure vessels

Pressurized water reactors

Recovery

High flux

Irradiated materials

Low flux

Matrix defects

Pressure vessel steels

Reactor Pressure Vessel

Solute cluster

Weldments

Alloy steel

Publication and Content Type

ref (subject category)

art (subject category)