Application of tungsten for plasma limiters in TEXTOR

• Three different types of W limiters were exposed in the TEXTOR plasma and the response of the plasma and materials performance of the limiters were investigated. 1. A W bulk limiter operated with preheating above 800 K withstood a plasma heat load of about similar to 20 MW/m(2) for a few seconds with some slight surface melting during the highest heat load shot. However, it was severely damaged when operated at around 500 K. 2. A C/W twin test limiter, half made of bulk W and the other half of graphite (EK-98) gave very useful information on how low- and high-Z materials behave under conditions of simultaneous utilization as PFM such as cross-contamination and the influence of a large mass difference on hydrogen reflection and deposition. 3. Two sets of main poloidal W limiters made of vacuum vapor sprayed (VPS)-W deposited on graphite (IG-430U) with a Re interlayer could absorb about 60% of the total convection heat and the ohmic plasma with a density as high as 5 x 10(13) cm(-3) was sustained. Most of the VPS-W coated limiters tolerated a heal load of similar to 20 MW/m(2). This series of W limiters experiments in TEXTOR has shown that W is applicable as a PFM, if its central accumulation is avoided by NBI and/or ICRH heating. Nevertheless, some concerns still remain, including difficulty of plasma startup, W behavior in higher temperature plasmas, and materials' selection.

Keyword

edge

Publication and Content Type

ref (subject category)

art (subject category)