Mechanical behaviour of SMC composites with toughening and low density additives
- Artikel/kapitelEngelska2003
Förlag, utgivningsår, omfång ...
-
Elsevier BV,2003
-
printrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:kth-22753
-
https://urn.kb.se/resolve?urn=urn:nbn:se:kth:diva-22753URI
-
https://doi.org/10.1016/s1359-835x(03)00155-6DOI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
QC 20100525
-
A new type of SMC material (Flex-SMC) developed for automotive exterior body panels has been investigated. Flex-SMC contains hollow glass micro-spheres and thermoplastic toughening additives. A conventional SMC (Std-SMC) was used as a reference material. Materials were tested in monotonic tension and compression. Stiffness degradation with strain as well as fracture toughness was determined. In situ SEM was used to study failure mechanisms. Flex-SMC has a density almost 20% lower than Std-SMC and has higher impact resistance. The damage threshold strain of the Flex-SMCs is higher than for Std-SMC. Flex-SMCs have more than twice the fracture toughness of Std-SMC. The major reason identified is that Flex-SMCs shows extensive fibre pullout.
Ämnesord och genrebeteckningar
-
moulding compound
-
mechanical properties
-
mechanical testing
-
short-fiber composites
-
bridging-law concepts
-
crack-growth
-
r-curves
-
damage
-
fracture
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Fernberg, S. P.
(författare)
-
Berglund, Lars A.KTH,Fiber- och polymerteknologi(Swepub:kth)u1wqz3r1
(författare)
-
KTHFiber- och polymerteknologi
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Composites. Part A, Applied science and manufacturing: Elsevier BV34:9, s. 875-8851359-835X1878-5840
Internetlänk
Hitta via bibliotek
Till lärosätets databas