Bistable defect in mega-electron-volt proton implanted 4H silicon carbide

• Epitaxial 4H-SiC n-type layers implanted at room temperature with a low fluence of mega-electron-volt protons have been measured by deep level transient spectroscopy (DLTS). The proton fluence of 1x10(12) cm(-2) creates an estimated initial concentration of intrinsic point defects of about 10(14) cm(-3) of which about 10% remain after the implantation and gives rise to deep states in the upper part of the band gap. Here, we investigate the samples prior to high-temperature annealing and a very complex spectrum is revealed. In particular, a bistable defect M is discovered having two DLTS peaks, M-1 and M-3 at E-C-0.42 and around E-C-0.75 eV, respectively, in one configuration and one peak, M-2 at E-C-0.70 eV in the other configuration. The charge dependent thermal activation energies for the transformation between the bistable defect peaks are 0.90 and 1.40 eV.

Ämnesord

NATURVETENSKAP  -- Fysik (hsv//swe)

NATURAL SCIENCES  -- Physical Sciences (hsv//eng)

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)