NiFeOx as a Bifunctional Electrocatalyst for Oxygen Reduction (OR) and Evolution (OE) Reaction in Alkaline Media

• This article reports the two-step synthesis of NiFeOx nanomaterials and their characterization and bifunctional electrocatalytic activity measurements in alkaline electrolyte for metal-air batteries. The samples were mostly in layered double hydroxide at the initial temperature, but upon heat treatment, they were converted to NiFe2O4 phases. The electrochemical behaviour of the different samples was studied by linear sweep voltammetry and cyclic voltammetry on the glassy carbon electrode. The OER catalyst activity was observed for low mass loadings (0.125 mg cm−2), whereas high catalyst loading exhibited the best performance on the ORR side. The sample heat-treated at 250 °C delivered the highest bi-functional oxygen evolution and reduction reaction activity (OER/ORR) thanks to its thin-holey nanosheet-like structure with higher nickel oxidation state at 250 °C. This work further helps to develop low-cost electrocatalyst development for metal-air batteries

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Kemiteknik -- Annan kemiteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Chemical Engineering -- Other Chemical Engineering (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Kemiteknik -- Kemiska processer (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Chemical Engineering -- Chemical Process Engineering (hsv//eng)

NATURVETENSKAP  -- Kemi -- Fysikalisk kemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Physical Chemistry (hsv//eng)

Nyckelord

Chemical Engineering

Kemiteknik

Kemi

Chemistry

Bi-functional catalyst

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)