TRIBOLOGY OF THREE RAILWAY BRAKE BLOCK MATERIALS TESTED AGAINST RAILWAYWHEEL AT LOW TEMPERATURES

QC 20190522
Three railway brake block materials, i.e. cast iron, sintered and organic composite, were tested against railway wheel at10, 3, -10, -20 and -30 °C using a pin-on-disc tribometer with regards to the friction and wear performance. At -10 and -20 °C, cast iron tests yielded very high wear losses both on pin and disc samples and low friction coefficient. The largeamount of graphite worn off from the cast iron sample acted as a lubricant. Friction and wear of sintered material arenot sensitive to the change of temperature. Disc sample tested against organic composite at -30 °C showed negativewear loss, indicating that materials were added onto the surface.

Bergseth, Ellen,1979-KTH,Maskinelement,Tribologi,System and Component Design(Swepub:kth)u1qevz2q (författare)
Olofsson, Ulf,1962-KTH,Tribologi,SKD(Swepub:kth)u10qpddv (författare)
KTHTribologi (creator_code:org_t)

Av författaren/redakt...: Lyu, Yezhe, 1987 ...; Bergseth, Ellen, ...; Olofsson, Ulf, 1 ...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Maskinteknik; och Tribologi

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.