Corrosion fatigue of austenitic cast iron Ni-Resist D5S and austenitic cast steel HK30 in argon and synthetic diesel exhaust at 800 degrees C

• To increase the understanding of the corrosion-fatigue mechanisms in two cast iron-alloys used in exhaust manifolds, low-cycle fatigue tests at 800 degrees C in argon and synthetic diesel exhaust as well as isothermal oxidation tests in the exhaust atmosphere are conducted. The corrosion impacts on the fatigue life of the materials are quantitatively evaluated from comparing the G-N curves, and examined from characterization through SEM, EDX, EBSD and EPMA. The materials show very different behaviors to the synergistic effect of corrosion and fatigue. Different theories have been suggested based on the findings.

Subject headings

TEKNIK OCH TEKNOLOGIER  -- Kemiteknik -- Korrosionsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Chemical Engineering -- Corrosion Engineering (hsv//eng)

Keyword

Corrosion fatigue

Low-cycle fatigue

Controlled atmosphere

High temperature

Cast iron-alloys

Publication and Content Type

ref (subject category)

art (subject category)