Delayed Hydride Cracking in Irradiated Zircaloy Cladding

STP1354

Artikel/kapitelEngelska2000

Förlag, utgivningsår, omfång ...

USA :ASTM International,2000
printrdacarrier

Nummerbeteckningar

LIBRIS-ID:oai:DiVA.org:kth-294489
https://urn.kb.se/resolve?urn=urn:nbn:se:kth:diva-294489URI
https://doi.org/10.1520/STP14307SDOI
https://urn.kb.se/resolve?urn=urn:nbn:se:kth:diva-244065URI

Kompletterande språkuppgifter

Språk:engelska
Sammanfattning på:engelska

Ingår i deldatabas

SwePubSwePub

Klassifikation

Ämneskategori:ref swepub-contenttype
Ämneskategori:kap swepub-publicationtype

Anmärkningar

QCR 20210518
QCR 20190227
Slow stable crack growth by a mechanism identified as a form of delayed hydride cracking has been studied on irradiated Zircaloy cladding. The background to the investigation was the formation of long axial cracks in defected fuel rods. Post-irradiation examination of such fuel rods has indicated that precipitation and subsequent cracking of hydrides at the tips of the long cracks has played an important role in the crack growth process. The present investigation conducted on irradiated cladding with hydrogen concentrations above about 500 ppm has demonstrated that a hydrogen-induced crack growth process can occur in such material. In the laboratory it was necessary to subject the samples to an overtemperature cycle in order to initiate crack growth after fatigue precracking. It was also observed that an incubation time on the order of 20 h was necessary before crack growth started. The crack growth rates were strongly dependent on the applied stress intensity factor K in a narrow range above a threshold value KIH, which was about 10 MPa√m, Stage I. The growth rate then reached a plateau value when it was independent of K, Stage II. This plateau value was about 10-6 m/s at 300°C and about 2 × 10-7 m/s at 200°C. This temperature dependence is consistent with a mechanism based on stress-induced diffusion of hydrogen at the stress concentration of the crack tip. Metallographic and fractographic observations suggest that the details of the mechanism can be best described as a localized reduction of fracture toughness due to reorientation of hydrides so that they become perpendicular to the applied stress in the region of the crack tip. This is somewhat in contrast to previous DHC mechanisms in which longer-range diffusion of hydrogen to one large hydride at the crack tip is usually modeled. The difference is that in the present case the hydride content is higher and therefore more hydrides are present.

Ämnesord och genrebeteckningar

TEKNIK OCH TEKNOLOGIER Materialteknik Annan materialteknik hsv//swe
ENGINEERING AND TECHNOLOGY Materials Engineering Other Materials Engineering hsv//eng
TEKNIK OCH TEKNOLOGIER Maskinteknik Teknisk mekanik hsv//swe
ENGINEERING AND TECHNOLOGY Mechanical Engineering Applied Mechanics hsv//eng
Zircaloy
delayed hydride cracking
crack growth
hydrides
irradiation effects
threshold stress intensity
Kärnenergiteknik
Nuclear Engineering
Hållfasthetslära

Biuppslag (personer, institutioner, konferenser, titlar ...)

Pettersson, KjellKTH,Mekanisk metallografi,Tidigare Institutioner (före 2005) (författare)
KTHSkolan för teknikvetenskap (SCI) (creator_code:org_t)

Sammanhörande titlar

Ingår i:Zirconium in the Nuclear Industry: Twelfth International SymposiumUSA : ASTM International, s. 340-355
Ingår i:Zirconium in the Nuclear IndustryUSA : ASTM International, s. 340-355

Internetlänk

Hitta via bibliotek

Zirconium in the Nuclear Industry: Twelfth International Symposium (Sök värdpublikationen i LIBRIS)

Till lärosätets databas

Hitta mer i SwePub

Av författaren/redakt...: Efsing, Pål, 196 ...; Pettersson, Kjel ...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Annan materialte ...

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Maskinteknik; och Teknisk mekanik

Artiklar i publikationen: Zirconium in ...

Av lärosätet: Kungliga Tekniska Högskolan

Sök utanför SwePub

Sök vidare i:: Google; Google Book Search; Google Scholar

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

LIBRIS.kb.se