Structural damage in ZnO bombarded by heavy ions

QC 20110218 19th International Conference on the Interaction of Ions with Surfaces, Zvenigorod, RUSSIA, AUG 21-25, 2009
The effect of implantation parameters on damage build-up in ZnO bombarded with Bi and Er ions is studied by Rutherford backscattering/channelling spectrometry. The results show that the damage accumulation behaviour in ZnO is different dramatically from that in other semiconductors. In particular, a variation of implantation parameters, such as collision cascade density, sample temperature and ion flux, has only a minor influence on the damage accumulation in the crystal bulk for the case of such heavy ions. Moreover, an intermediate damage peak, between the surface and bulk defect peaks, is observed for all the irradiation conditions studied. The cascade density affects the behaviour of this intermediate peak with increasing ion dose.

Titov, A. I. (författare)
Karaseov, P. A. (författare)
Kucheyev, S. O. (författare)
Hallén, AndersKTH,Mikroelektronik och tillämpad fysik, MAP(Swepub:kth)u11ywmz1 (författare)
Kuznetsov, A. Yu. (författare)
Svensson, B. G. (författare)
Pathak, A. P. (författare)
KTHMikroelektronik och tillämpad fysik, MAP (creator_code:org_t)

Av författaren/redakt...: Azarov, A. Yu.; Titov, A. I.; Karaseov, P. A.; Kucheyev, S. O.; Hallén, Anders; Kuznetsov, A. Yu ...; visa fler...; Svensson, B. G.; Pathak, A. P.; visa färre...

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.