Degree of Undercooling and Contact Angle of Pure Iron at 1 933 K on Single-crystal Al2O3, MgO, and MgAl2O4 under Argon Atmosphere with Controlled Oxygen Partial Pressure

QC 20110304 Conference on Cutting Edge of Studies in Inclusions and Precipitates Behavior Related to Microstructure Control, Kumamoto, JAPAN, SEP, 2008
Solid or molten oxides are considered to act as nucleation sites during continuous steel casting. The influence of the kind of oxide crystal and atmospheric oxygen partial pressure on the degree of undercooling and contact angle of pure molten iron on oxide substrates was measured by the sessile drop method. On Al2O3 and MgAl2O4 substrates, we found that the change in the degree of undercooling was dependent on the existence of a reaction layer and its thickness. On an MgO substrate, since no reaction layer formed, the degree of undercooling was small and was governed by the lattice misfit parameter. The equilibrium contact angle of a molten iron drop on the FeAl2O4 layer formed between the Al2O3 substrate and drop was about 100 degrees; a similar contact angle was obtained on MgAl2O4. The contact angle on MgO changed during observation due to the evaporation of Mg.

TEKNIK OCH TEKNOLOGIER Materialteknik Metallurgi och metalliska material hsv//swe
ENGINEERING AND TECHNOLOGY Materials Engineering Metallurgy and Metallic Materials hsv//eng
undercooling
contact angle
oxygen partial pressure
oxides
nucleation
Metallurgical process engineering
Metallurgisk processteknik

Ingår i:ISIJ International: Iron and Steel Institute of Japan49:7, s. 985-9910915-15591347-5460

Av författaren/redakt...: Shibata, Hiroyuk ...; Watanabe, Yusuke; Nakajima, Keiji; Kitamura, Shin-y ...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Metallurgi och m ...

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.