Bigdeli, Sedigheh,1984Chalmers,Chalmers tekniska högskola,Chalmers University of Technology (författare)

Strategies for High-Temperature Corrosion Simulations of Fe-Based Alloys Using the Calphad Approach : Part I

QC 20220323
The environmental degradation of materials at high temperatures limits the useful life of different industrial components and hinders the development of more economical and environmentally friendly processes for the energy production. Despite the importance of this phenomena, a model to predict lifetime of materials that degrade due to high-temperature corrosion has up till now been lacking due to limitations of the computational possibilities and the complex nature of oxidation. In the present work we develop some strategies to model high-temperature corrosion in Fe-based alloys using the Calphad (Calculation of Phase Diagrams) approach. It is proposed that kinetic-based simulations for oxidation of Al and Cr can accurately represent the lifetime of the protective layers in FeCrAl and FeCr alloys at different temperatures in air. The oxide systems are in addition investigated by equilibrium calculations. The corrosion mechanisms of FeCr and FeCrAl alloys are discussed based on theoretical and experimental knowledge.

TEKNIK OCH TEKNOLOGIER Materialteknik Metallurgi och metalliska material hsv//swe
ENGINEERING AND TECHNOLOGY Materials Engineering Metallurgy and Metallic Materials hsv//eng
TEKNIK OCH TEKNOLOGIER Materialteknik Annan materialteknik hsv//swe
ENGINEERING AND TECHNOLOGY Materials Engineering Other Materials Engineering hsv//eng
TEKNIK OCH TEKNOLOGIER Kemiteknik Korrosionsteknik hsv//swe
ENGINEERING AND TECHNOLOGY Chemical Engineering Corrosion Engineering hsv//eng
CALPHAD
DICTRA modeling
FeCr/FeCrAl alloys
high temperature oxidation
Aluminum alloys
Aluminum corrosion
Binary alloys
Chromium alloys
Green manufacturing
High temperature corrosion
Ternary alloys
Calculation of phase diagrams
Corrosion mechanisms
Energy productions
Environmentally friendly process
Equilibrium calculation
Experimental knowledge
Industrial components
Protective layers
Iron alloys

Kjellqvist, L.Thermo-Calc Software AB, Ra ̊sundava ̈gen 18, 169 67 Solna, Sweden (författare)
Naraghi, R.Thermo-Calc Software AB, Ra ̊sundava ̈gen 18, 169 67 Solna, Sweden (författare)
Höglund, LarsKTH,Strukturer,Thermo-Calc Software AB, Råsundavägen 18, 169 67 Solna, Sweden,Kungliga Tekniska Högskolan (KTH),Royal Institute of Technology (KTH)(Swepub:kth)u1bpg6iz (författare)
Larsson, HenrikKTH,Strukturer,Thermo-Calc Software AB, Råsundavägen 18, 169 67 Solna, Sweden,Kungliga Tekniska Högskolan (KTH),Royal Institute of Technology (KTH)(Swepub:kth)u1z5mmxu (författare)
Jonsson, Torbjörn,1970Chalmers,Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)tj (författare)
ChalmersChalmers tekniska högskola (creator_code:org_t)

Ingår i:Journal of Phase Equilibria and Diffusion: Springer Nature42:3, s. 403-4181547-70371863-7345

Av författaren/redakt...: Bigdeli, Sedighe ...; Kjellqvist, L.; Naraghi, R.; Höglund, Lars; Larsson, Henrik; Jonsson, Torbjör ...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Metallurgi och m ...

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Annan materialte ...

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Kemiteknik; och Korrosionsteknik

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.