Passivation characteristics of ultra-thin 316L foil in NaCl solutions

• Electrochemical behaviour and passive film characteristics of an ultra-thin 316L foil with a thickness of 20 ??m in 3.5 wt.% NaCl solution were investigated using multiple techniques, focusing on the effect of microstructure, the applied potential, and the pH of the solution. The microstructure contains mainly fine grains ( ???4 ??m) with high-angle boundaries and preferential orientation of (220), and no MnS inclusion was detected. The electrochemical measurements show a significantly higher breakdown potential and lower passive current density for the 316L foil than traditional wrought 316L. The surface analyses using angle-resolved X-ray photoelectron spectroscopy (ARXPS) and time-of-flight secondary ion mass spectroscopy (TOF-SIMS) reveal that, compared to the wrought material, both the inner and out parts of the passive film on the 316L foil are more enriched in Cr- and Mo-oxides. The microstructure favourable for elemental diffusion and the absence of MnS inclusion facilitate the formation of a continuous compact Cr- and Mo-rich passive film, which effectively retards corrosion in NaCl solution and remains stable in acidic solution (pH 2) or at high polarised potential up to 600 mV vs Ag/AgCl. ?? 2022 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology. This is an open access article under the CC BY license ( http://creativecommons.org/licenses/by/4.0/ )

Ämnesord

NATURVETENSKAP  -- Fysik -- Annan fysik (hsv//swe)

NATURAL SCIENCES  -- Physical Sciences -- Other Physics Topics (hsv//eng)

Nyckelord

Ultra-thin 316L foil

Passive film

Pitting corrosion

XPS

TOF-SIMS

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)