Growth, coalescence, and electrical resistivity of thin Pt films grown by dc magnetron sputtering on SiO2
- Artikel/kapitelEngelska2008
Förlag, utgivningsår, omfång ...
-
Elsevier BV,2008
-
printrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:kth-33083
-
https://urn.kb.se/resolve?urn=urn:nbn:se:kth:diva-33083URI
-
https://doi.org/10.1016/j.apsusc.2008.05.335DOI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
QC 20110524
-
Ultra thin platinum films were grown by dc magnetron sputtering on thermally oxidized Si (100) substrates. The electrical resistance of the films was monitored in situ during growth. The coalescence thickness was determined for various growth temperatures and found to increase from 1.1 nm for films grown at room temperature to 3.3 nm for films grown at 400 degrees C. A continuous film was formed at a thickness of 2.9 nm at room temperature and 7.5 nm at 400 degrees C. The room temperature electrical resistivity decreases with increased growth temperature, while the in-plain grain size and the surface roughness, measured with a scanning tunneling microscope (STM), increase. Furthermore, the temperature dependence of the film electrical resistance was explored at various stages during growth.
Ämnesord och genrebeteckningar
-
in situ resistivity
-
coalescence
-
thin film
-
magnetron sputtering
-
STM
-
TECHNOLOGY
-
TEKNIKVETENSKAP
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Arnalds, U. B.
(författare)
-
Ingason, A. S.
(författare)
-
Gylfason, Kristinn B.KTH,Mikrosystemteknik(Swepub:kth)u1v3y7u7
(författare)
-
Johnsen, K.
(författare)
-
Olafsson, S.
(författare)
-
Gudmundsson, Jon TomasUniversity of Iceland, Iceland(Swepub:kth)u1q27a34
(författare)
-
KTHMikrosystemteknik
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Applied Surface Science: Elsevier BV254:22, s. 7356-73600169-43321873-5584
Internetlänk
Hitta via bibliotek
Till lärosätets databas