Graded Anisotropy FePtCu Films

• The fabrication and subsequent analysis of continuously graded anisotropy films are discussed. During deposition, a compositional gradient is first achieved by varying the Cu concentration from Cu-rich (Fe53Pt47)(70)Cu-30 to Cu-free Fe53Pt47. The anisotropy gradient is then realized after thermal post-annealing, and by utilizing the strong composition dependence of the low-anisotropy (A1) to high-anisotropy (L1(0)) ordering temperature. The magnetic properties are investigated by surface sensitive magneto-optical Kerr effect and alternating gradient magnetometer (AGM) measurements. AGM first-order reversal curve (FORC) measurements are employed in order to provide a detailed analysis of the reversal mechanisms, and therefore the induced anisotropy gradient. At low annealing temperatures, the FORC measurements clearly indicate the highly coupled reversal of soft and hard phases. However, significant interdiffusion results in virtually uniform films at elevated annealing temperatures. Additionally, the A1 to L1(0) ordering process is found to depend on the film thickness.

Ämnesord

NATURVETENSKAP  -- Fysik -- Den kondenserade materiens fysik (hsv//swe)

NATURAL SCIENCES  -- Physical Sciences -- Condensed Matter Physics (hsv//eng)

Nyckelord

FePtCu thin films

first-order reversal curve (FORC) measurements

graded anisotropy films

magnetic reversal mechanism

TECHNOLOGY

TEKNIKVETENSKAP

magnetism

spintronics

graded materials

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)