Highly strained InGaAs/GaAs multiple quantum-wells for laser applications in the 1200-1300-nm wavelength regime

Uppdaterad från submitted til published: 20101001. QC 20101001
We report on metalorganic vapor-phase epitaxy growth optimization and properties of highly strained InGaAs/GaAs quantum-well (QW) structures with emission wavelength beyond 1200 nm. It is observed that a sufficiently high V/III ratio in combination with low growth temperature is critical for preserved layer integrity when increasing the strain. Multiple QWs with up to five wells are realized without any degradation in photoluminescence intensity or broad-area laser performance at an emission wavelength of 1240 nm with threshold current density below 70 A/cm(2) per well.

Berggren, JesperKTH,Mikroelektronik och Informationsteknik, IMIT(Swepub:kth)u13fhsee (författare)
Goldman, Peter M.O.KTH,Mikroelektronik och Informationsteknik, IMIT(Swepub:kth)u1mgkg8w (författare)
Hammar, MattiasKTH,Mikroelektronik och Informationsteknik, IMIT(Swepub:kth)u1jfzgcj (författare)
KTHMikroelektronik och Informationsteknik, IMIT (creator_code:org_t)

Ingår i:Applied Physics Letters: AIP Publishing87:7, s. 071104-0003-69511077-3118

Av författaren/redakt...: Sundgren, Petrus; Berggren, Jesper; Goldman, Peter M ...; Hammar, Mattias

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.