Effect of nuclear scattering damage at the SiO2/SiC and Al2O3/SiC interface : A radiation hardness study of dielectrics

• The radiation hardness of Al2O3 as a dielectric for SiC surface passivation is studied and compared to SiO2 for potential application in radiation hard SiC devices. SiO2 is deposited on 4H-SiC by PECVD and post annealed in N2O, whereas Al2O3 is deposited by atomic layer deposition (ALD). The oxides are bombarded with Ar ions in an energy range to produce maximum damage near the oxide/SiC interface. Metal-insulator-semiconductor structures are prepared and their dielectric characteristics are analyzed using capacitance-voltage measurements. Additionally, the effect of the interface damage on surface recombination is studied using the optical free carrier absorption method for the same samples. The results indicate that the SiO2/SiC interface is significantly affected at 1×1011 cm-2 fluence of Ar ions, however, the dielectric properties of Al2O3/SiC interface remain unaffected even for ten times higher fluences. Similar observations are made for the surface recombination measurements.

Subject headings

TEKNIK OCH TEKNOLOGIER  -- Elektroteknik och elektronik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Electrical Engineering, Electronic Engineering, Information Engineering (hsv//eng)

Keyword

4H-SiC

High-k Dielectrics

Interface Damage

MIS

Radiation Hardness

Publication and Content Type

ref (subject category)

kon (subject category)