Microwave properties of AgTa0.5Nb0.5O3 thin film varactors on various substrates

• 400nm thick AgTa0.5Nb0.5O3 (ATN) films have been sintered by pulsed laser deposition technique on LaAlO3 (001), sapphire (Al2O3-01 (1) under bar2, r-cut) single crystal substrates and Coming 7059 Glass. Photolithography and metal lift-off technique were used to fabricate tunable Coplanar Waveguide Interdigital Capacitors (CPWIDCs). On-wafer test of varactors was performed with microwave network analyzer and G-S-G microwave probe. ATN/LaAlO3 capacitors demonstrated the highest tunability (similar to 5.8%@20GHz), ATN/Glass showed the best flat dispersion (similar to 3.9%) and ATN/ Al2O3 showed the lowest loss tangent (similar to 0.06@20GHz) in the microwave range from 1 to 40 GHz.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Elektroteknik och elektronik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Electrical Engineering, Electronic Engineering, Information Engineering (hsv//eng)

Nyckelord

Ceramic thin film

Coplanar waveguides

Scattering parameters

Voltage tunable devices

Electrical engineering, electronics and photonics

Elektroteknik, elektronik och fotonik

Publikations- och innehållstyp

ref (ämneskategori)

kon (ämneskategori)