Local switching properties of dense nanocrystalline BaTiO3 ceramics

QC 20120305
The switching properties of dense BaTiO3 ceramics with 50 nm average grain size were investigated at local scale by piezoresponse force microscopy. Large areas with low piezoelectrical activity beside islands with strong piezoresponse were found. The application of electric fields induces stable domain structures and changes in the polarization state far away from the probing area, probably via trans-granular dipole interactions. Piezoelectric hysteresis loops were recorded on various positions, even in regions with initial zero piezoresponse, which possibly showed a superparaelectric behavior. The results are incontestable proof that 50 nm BaTiO3 ceramics retain ferroelectricity at a local scale.

Harnagea, C. (författare)
Nanni, P. (författare)
Testino, A. (författare)
Buscaglia, M. T. (författare)
Buscaglia, V. (författare)
Viviani, M. (författare)
Zhao, Zhe,1973-Department of Physical Inorganic and Structural Chemistry, Stockholm University(Swepub:kth)u1qw3zev (författare)
Nygren, M. (författare)
Department of Physical Inorganic and Structural Chemistry, Stockholm University (creator_code:org_t)

Ingår i:Applied Physics Letters: AIP Publishing84:13, s. 2418-24200003-69511077-3118

Av författaren/redakt...: Mitoseriu, L.; Harnagea, C.; Nanni, P.; Testino, A.; Buscaglia, M. T.; Buscaglia, V.; visa fler...; Viviani, M.; Zhao, Zhe, 1973-; Nygren, M.; visa färre...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Keramteknik

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.