Grain-size effects on the ferroelectric behavior of dense nanocrystalline BaTiO3 ceramics

Zhao, Zhe,1973-Department of Physical Inorganic and Structural Chemistry, Stockholm University (författare)

QC 20120302
A progressive reduction of tetragonal distortion, heat of transition, Curie temperature, and relative dielectric constant has been observed on dense BaTiO3 ceramics with grain size decreasing from 1200 to 50 nm. The correlations between grain size, extent of tetragonal distortion, and ferroelectric properties strongly support the existence of an intrinsic size effect. From the experimental trends the critical size for disappearance of ferroelectricity has been evaluated to be 10-30 nm. The strong depression of the relative permittivity observed for the nanocrystalline ceramics can be ascribed to the combination of the intrinsic size effect and of the size-dependent "dilution" effect of a grain boundary "dead" layer.

Buscaglia, V. (författare)
Viviani, M. (författare)
Buscaglia, M. T. (författare)
Mitoseriu, L. (författare)
Testino, A. (författare)
Nygren, M. (författare)
Johnsson, M. (författare)
Nanni, P. (författare)
Department of Physical Inorganic and Structural Chemistry, Stockholm University (creator_code:org_t)

Ingår i:Physical Review B. Condensed Matter and Materials Physics: American Institute of Physics (AIP)70:21098-01211550-235X

Av författaren/redakt...: Zhao, Zhe, 1973-; Buscaglia, V.; Viviani, M.; Buscaglia, M. T.; Mitoseriu, L.; Testino, A.; visa fler...; Nygren, M.; Johnsson, M.; Nanni, P.; visa färre...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Keramteknik

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.